Pengaruh Parameter Proses Terhadap Kekuatan Tarik dan Impak Pada Pengelasan Disimilar Antara Material Baja AH36 dan Stainless Steel 304

Sudibyo, Josua Hamonangan (2026) Pengaruh Parameter Proses Terhadap Kekuatan Tarik dan Impak Pada Pengelasan Disimilar Antara Material Baja AH36 dan Stainless Steel 304. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6007212017-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (14MB) | Request a copy

Abstract

Penggabungan baja berbeda jenis merupakan salah satu aspek penting dalam perindustrian pada zaman modern ini. Salah satu aplikasi penggunaan teknologi ini adalah di tangki penyimpanan di tangki muatan kapal bermuatan cairan kimia. Baja AH36 dan Stainless Steel 304 adalah jenis material yang umum digunakan pada konstruksi kapal tanker bermuatan kimia. Pada pengelasan berbeda material, pengelasan sering menjadi kesulitan karena peleburan elektrode dengan kedua material tidak terbentuk sempurna. Pada penelitian ini faktor yang bisa mempengaruhi hasil pengelasanan kedua material tersebut, yaitu jenis kawat, arus pengelesan dan voltase pengelasan akan dianalisa. Setelah itu, spesimen akan di-analisa menggunakan uji tarik, uji impact, dan hardness pada kondisi optimal. Dari hasil pengujian, dilakukan perhitungan optimalisasi menggunakan Grey Relational Analysis (GRA) danTaguchi untuk menemukan faktor yang berpengaruh signifikan dan kombinasi level yang memberi hasil paling optimal. Dari hasil optimalisasi, ditemukan bahwa faktor yang berpengaruh signifikan adalah arus pengelasan dan jenis elektrode yang digunakan. Kombinasi level yang memberi hasil paling optimal adalah kawat E7016L, arus pengelasan 85 A dan voltase pengelasan 110 V yang memberikan hasil uji tarik 97.781 N/mm2 dan uji impak sebesar 75.679 j. Hasil distribusi kekerasan menggunakan metode vickers menunjukkan bahwa kekerasan yang rata – rata lebih besar ada pada bagian pengelasan root dan kekerasan dengan rata – rata lebih kecil ada pada bagian base metal baja AH36.
================================================================================================================================
A Merger of different type of steel are one of the very important aspects in today’s modern industrial era. One of merged steel applications that are often used are in cargo tanks used in tanker ships that carried corrosive chemical liquid. AH36 steel & stainless steel are two types that are used on chemical tanker construction. On dissimilar metal welding, a lot problems occur because of not completed formed or not completed smelting of the filler metal. On this thesis, factors that may affect the final welding of these 2 different steels which is electrode type, welding current and welding voltage will be analyzed closely. Afterwards, specimens of welded steel were tested using tensile strength test, impact test & hardness checking on the optimum condition. The results of the testing are optimized using Grey Relational Analysis (GRA) and Taguchi to find out types and level of factors that produce optimum results of impact & tensile strength. From the optimalization results, it can be concluded that factors which have a significant influence on the welding are electrode type and welding current. Levels that give optimum results are E7016L electrode, 85 A welding current and 110V welding voltage that gives tensile strength result of 97.781 N/mm2 and impact result of 75.679 j. The Results of Vickers hardness testing shows that the bigger value occurs on the root welding, while the smaller value occurs on the AH36 base metal area.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	AH 36 Steel, Stainless Steel 304, Welding & Optimalization
Subjects:	T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21101-(S2) Master Thesis
Depositing User:	Josua Hamonangan Sudibyo
Date Deposited:	02 Feb 2026 05:18
Last Modified:	02 Feb 2026 05:18
URI:	http://repository.its.ac.id/id/eprint/131735

Actions (login required)

View Item