Pengaruh Variasi Interlocking Structure Orientation Dan Jumlah Lapisan Beam Layer Count Pada Sambungan Interlock Hasil 3d Printing Berbahan Pla

Prastiyo, Panggih (2026) Pengaruh Variasi Interlocking Structure Orientation Dan Jumlah Lapisan Beam Layer Count Pada Sambungan Interlock Hasil 3d Printing Berbahan Pla. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038211056_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (6MB) | Request a copy

Abstract

Teknologi 3D Print Multimaterial Additive Manufacturing (MM-AM) merupakan metode inovatif dalam mencetak objek dengan menggunakan berbagai jenis material secara bersamaan dan membuka pintu untuk menciptakan struktur yang kompleks dan fungsional. Meskipun demikian, terdapat permasalahan potensial terkait ikatan yang lemah antar- material yang dapat mempengaruhi kekuatan dan kualitas produk hasil cetakan. Penelitian ini bertujuan untuk mengatasi tantangan tersebut dengan memanfaatkan fitur interlock sebagai solusi. Dalam konteks ini, interlock merujuk pada desain khusus yang memungkinkan material-material yang berbeda saling terkunci satu sama lain, meningkatkan daya tahan dan integritas struktural produk akhir. Artikel ini menyajikan analisis mendalam terhadap permasalahan ikatan lemah pada 3D Print Multi Material AM dan mengusulkan strategi implementasi fitur interlock sebagai solusi efektif. Penelitian ini bertujuan untuk membandingkan performa variasi Beam layer count dan interlocking structure orientation pada sambungan interlock . fitur interlock mencakup tools khusus yang disediakan oleh software Ultimaker Cura 5.4. Melalui serangkaian eksperimen dan analisis, studi ini mengevaluasi kekuatan ikatan, dan ketahanan struktural dari kedua pendekatan tersebut. Hasil eksperimen tersebut memberikan wawasan tentang efektivitas masing-masing metode dalam meningkatkan kualitas dan keandalan spesimen yang dihasilkan. Untuk mengetahui nilai kekuatan ketahanan ikatan interlock maka akan digunakan metode uji tarik dari produk MM- AM filamen PLA yang difabrikasi melalui parameter yang sudah ditentukan dengan cara spesimen dicetak berdasarkan standar uji ASTM D638 type 1 dan untuk mengetahui pengaruh dari parameter interlock yang ada pada fitur tersebut. Hasil yang diharapkan pada penelitian ASTM D638 type 1 adalah untuk mengetahui tingkat kekuatan tarik maksimum dari spesimen uji. Serta diharapkan hasil dari penelitian ini dapat dijadikan patokan dalam penggunaan fitur interlock dan dapat diimplementasikan pada produk cetak dengan ruang lingkup yang lebih luas.
======================================================================================================================================
Multimaterial 3D Printing Additive Manufacturing (MM-AM) technology is an innovative method for printing objects using various materials simultaneously, allowing for the creation of complex and functional structures. However, potential issues related to weak inter-material bonds may affect the strength and quality of the printed products. This study aims to address these challenges by utilizing interlock features as a solution. In this context, "interlock" refers to a specialized design that enables different materials to lock into one another, enhancing the durability and structural integrity of the final product. This article provides a comprehensive analysis of weak bonding issues in MM-AM and proposes the implementation of interlock features as an effective solution. The research aims to compare the performance of variations in Beam layer count number and angles on interlock joints. The interlock feature is implemented using specialized tools provided by Ultimaker Cura 5.4 software. Through a series of experiments and analyses, this study evaluates the bonding strength and structural durability of these approaches. The experimental results offer insights into the effectiveness of each method in improving the quality and reliability of the printed specimens. To assess the bonding strength of interlock joints, tensile testing is used on MM-AM PLA filament products, manufactured with predefined parameters according to ASTM D638 Type 1 testing standards. This approach highlights the increasing sophistication of 3D printing technologies, particularly in enhancing material performance and addressing challenges in multi-material additive manufacturing

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Additive Manufacturing, Dual Extruder, Interlocking, Ultimaker Cura,Additive Manufacturing, Dual Extruder, Interlocking, Ultimaker Cura
Subjects:	T Technology > TS Manufactures > TS171 Product design T Technology > TS Manufactures > TS183 Manufacturing processes. Lean manufacturing.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Panggih Tri Prastiyo
Date Deposited:	03 Feb 2026 10:10
Last Modified:	03 Feb 2026 10:10
URI:	http://repository.its.ac.id/id/eprint/131900