Modifikasi Membran Cellulose Acetate/Polyethylene Glycol (CA/PEG) Dengan Nanopartikel Anorganik Untuk Proses Desalinasi

Alifiyanti, Pitsyah Alifiyanti and Priambodo, Krisna Dimas (2016) Modifikasi Membran Cellulose Acetate/Polyethylene Glycol (CA/PEG) Dengan Nanopartikel Anorganik Untuk Proses Desalinasi. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2312100005_2312100126-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Perkembangan teknologi desalinasi amat penting dalam upaya memenuhi kebutuhan air di masa depan. Tujuan dari penelitian ini adalah untuk menciptakan membran desalinasi air laut dari cellulose acetate (CA) yang dicampurkan dengan polyethylene glycol (PEG) menghasilkan membran CA/PEG. Salah satu cara untuk meningkatkan kinerja membran desalinasi adalah dengan meningkatkan hidrofilisitas membran. Dalam penelitian ini (0; 0.0125; 0.025; 0.075; 0,05) gram CNT dan (0; 0.5: 0.75: 1: 1.25) 8) sovent TiO» ditambahkan pada membran CA/PEG guna meningkatkan hidrofilisitas membran tersebut. Hasil penelitian menunjukkan bahwa hidrofilisitas dan rijeksi garam membran CA/PEG meningkat dengan penambahan CNT dari 0.0125 sampai 0.05 gram. Sedangkan pada penambahan TiO» pada membran CA/PEG, hidrofilisitas membran dan rijeksi garam naik hingga penambahan TiO) sebesar 1 8/5 sovwen dan menurun dengan semakin bertambahnya TiO, yang ditambahkan. Hasil rijeksi garam dan fluks terbaik diperoleh dari hasil percobaan dengan membran CPT 3 (CA/PEG/TiO:, 80/20/1 8/1 sovent), yaitu 48,302 % rijeksi garam dan fluks 111,81 L/m?.hr.
=======================================================================================================================================
Development of desalination technologies is very important for fulfilling future water demand. The objective of this research is to synthesize membrane for desalination of saline water from cellulose acetate (CA) by blending with polyethylene glycol (PEG) resulting CA/PEG membrane. One way to improve desalination membrane performance is to increase the its hydrophilicity . In this study (0; 0.0125; 0.025: 0.075: 0.05) grams of CNT and (0; 0.5; 0,75; 1; 1,25) 8/1 sotvent Of TiO» is added to the membrane CA/PEG in order to improve the hydrophilicity of the membrane . The results showed that the hydrophilicity and salt rejection of membrane CA/PEG increases with the addition of CNTs from 0,0125 to 0,05 grams . While the addition of TiO» membranes CA/PEG , membrane hydrophilicity and salt rejection of TiO. membrane increased by the addition of 1 8/, seven and decreases with further addition of TiO2. Results salt rejection and the best flux obtained from experiments with membrane CPT 3 ( CA/PEG/ TiO? 80/20/1 g/1.sovent ) , With salt rejection at 48.302 % and flux of 111.81 L/m2.hr .

Item Type:	Thesis (Other)
Additional Information:	RSK 660.297 8 Ali m 2016 3100016067006 (WEEDING)
Uncontrolled Keywords:	Desalinasi, Selulosa, PEG, TiO2, Reserve osmosis
Subjects:	Q Science > QD Chemistry > QD320 Cellulose. Hydrolysis T Technology > TP Chemical technology T Technology > TP Chemical technology > TP155.7 Chemical processes.
Divisions:	Faculty of Industrial Technology > Chemical Engineering > 24201-(S1) Undergraduate Thesis
Depositing User:	Anis Wulandari
Date Deposited:	26 Feb 2026 03:31
Last Modified:	26 Feb 2026 03:46
URI:	http://repository.its.ac.id/id/eprint/132630

Actions (login required)

View Item