Sintesis Karbon/Zeolit (KZ) Termodifikasi Nitrogen Dengan Aktivator K2CO3 Sebagai Material Penyimpan Hidrogen Dengan Variasi Rasio K2CO3/Kz Termodifikasi Nitrogen

Kendra, Ricky Evan (2018) Sintesis Karbon/Zeolit (KZ) Termodifikasi Nitrogen Dengan Aktivator K2CO3 Sebagai Material Penyimpan Hidrogen Dengan Variasi Rasio K2CO3/Kz Termodifikasi Nitrogen. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211440000111-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (10MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk melakukan aktivasi pada Karbon/Zeolit (KZ) termodifikasi Nitrogen dengan activator K:CO: yang digunakan sebagai material penyimpan hidrogen. KZ termodifikasi nitrogen disintesis dengan metode impregnasi basah disertai karbonisasi. Proses aktivasi dengan variasi rasio K:CO: (g)/KZ (g) termodifikasi nitrogen = 2; 3 dan 4 dilakukan untuk mengatur pembentukan mikropori yang sesuai untuk penyimpanan hidrogen. Hasil penelitian menunjukkan aktivasi KZ termodifikasi nitrogen paling optimum didapat pada rasio 2,0 dengan luas permukaan dan volume mikropori masing-masing sebesar 352,789 m'/g dan 0,172 cc/g. KZ termodifikasi nitrogen sebelum dan setelah proses aktivasi diuji kapasitas penyimpanan H» menggunakan metode gravimetri dengan laju alir sebesar 20 mL/menit. Pengukuran kapasitas penyimpanan H» pada KZ termodifikasi nitrogen sebelum dan setelah proses aktivasi dengan rasio K2xCO3/KZ = 2 dilakukan pada suhu dan tekanan ruang dengan hasil secara berturut-turut sebesar 2,232% berat dan 4 442 berat.
=======================================================================================================================================
The aim of this research to activated nitrogen-modified carbon/zeolite (KZ) using K2CO3 activator as material for hydrogen storage. The nitrogen-modified KZ was synthesized via impregation method followed by carbonization. In this research, activation process was conducted at variations of K2CO3 (g)/ KZ (g) weight ratio of 2; 3 and 4 in order to control the formation of micropores which suitable for hydrogen storage. The result shows that K2CO; (g)/ KZ (g) weight rasio of 2 was the optimum ratio, which achieved specific surface area and micropores volume were 352.789 m'/g and 0.1722 cc/g, respectively. The hydrogen-storing capacity of nitrogenmodified KZ before and after activation was measured by using the gravimetric method at hydrogen flow of 20 mL/min. The result showed that the hydrogen adsorption capacity enhanced from 2.232% (wt) to 4.442% (wt) for nitrogen modified KZ after activation with K»CO3 at weight ratio of K2CO3/KZ ratio 2.

Item Type:	Thesis (Other)
Additional Information:	RSKi 549.68 Ken s-1 2018 3100018077627 (WEEDING)
Uncontrolled Keywords:	Karbon/Zeolit, Nitrogen, K₂CO₃, Penyimpanan hidrogen
Subjects:	T Technology > TP Chemical technology > TP159.M6 Zeolites
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Anis Wulandari
Date Deposited:	13 Apr 2026 04:15
Last Modified:	13 Apr 2026 04:15
URI:	http://repository.its.ac.id/id/eprint/132781