Pengaruh Variasi Rasio Templat Organik Ekstrak Lerak (SAPINDUS RARAK) Pada Sintesis Material Silika Mesopori Sebagai Adsorben Metilen Biru Dalam Air.

Putri, Ilda Zahra Karunia (2022) Pengaruh Variasi Rasio Templat Organik Ekstrak Lerak (SAPINDUS RARAK) Pada Sintesis Material Silika Mesopori Sebagai Adsorben Metilen Biru Dalam Air. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211840000065-UNDERGRADUATE_THESIS.pdf Restricted to Repository staff only Download (2MB)

Abstract

Metilen biru dalam air menyebabkan berbagai masalah pada kelangsungan ekosistem dan juga kesehatan masyarakat sekitar. Salah satu metode yang dianggap lebih mudah untuk menghilangkan metilen biru adalah adsorpsi. Penelitian ini bertujuan untuk mengetahui pengaruh dari konsentrasi templat organic ekstrak lerak (sapindus rarak) pada sintesis adsorben silika mesopori pada aplikasi adsorpsi metilen biru. Material silika mesopori disintesis dengan bahan natrium silikat sebagai prekursor dan ekstrak lerak sebagai templat organik dengan metode hidrotermal pada suhu 100 °C selama 24 jam. Hasil karakterisasi material silika mesopori memiliki fasa amorf dibuktikan dari difraktogram XRD. Spektra FTIR menunjukkan pita serapan pada bilangan gelombang 1090, 796, dan 470 cm−1 yang merupakan ciri-ciri kerangka bahan berbasis silika. Morfologi permukaan silika mesopori memiliki bentuk partikel yang bulat dan hampir seragam dengan ukuran partikel 1,85 μm. Karakterisasi adsorpsi-desorpsi N2 menujukan bahwa material berjenis mesopori dengan ukuran pori pada kisaran ±2 nm, luas permukaan BET 137,85-408,61 m2/g dan luas permukaan mesopori 96,61-151,99 m2/g. Material silika mesopori menunjukkan hasil yang paling optimum dengan nilai kapasitas adsorpsi maksimum sebesar 38,46 mg/g.===================================================================================================================================
Methylene blue in water causes various problems for the sustainability of the ecosystem and also the health of the surrounding community. One of the easier methods to remove metylene blue is adsorption. This study aims to determine the effect of the concentration of sapindus rarak extract organic template on the synthesis of mesoporous silica adsorbent in the adsorption application of metylene blue. Mesoporous silica material was synthesized with sodium silicate as precursor and sapindus rarak extract as organic template by hydrothermal method at 100 °C for 24 hours. The results of the characterization of the mesoporous silica material having an amorphous phase were proven from the XRD diffractogram. The FTIR spectra showed absorption bands at the wavenumber 1090, 796, dan 470 cm−1 which are the characteristic of the framework of silica-based materials. The surface morphology of mesoporous silica shows a spherical and almost uniform particle shape with a particle size of 1.85 μm. The adsorption-desorption characterization of N2 show that the material was mesoporous with a pore size in the range of ±2 nm, a BET surface area of 137.85-408.61 m2/g and a mesoporous surface area of 96.61-151.99 m2/g. Mesoporous silica material showed the most optimum results with a maximum adsorption capacity of 38.46 mg/g.

Item Type:	Thesis (Other)
Additional Information:	RSKi 546.683 Put p-1 2022
Uncontrolled Keywords:	Silika mesopori, Metilen Biru, Adsorpsi, Lerak, Adsorben. Mesoporous Silica, Methylene Blue, Adsorption, Sapindus Rarak, Adsorbent.
Subjects:	T Technology > TP Chemical technology > TP245.S5 Silica gel.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	06 May 2026 06:07
Last Modified:	06 May 2026 06:07
URI:	http://repository.its.ac.id/id/eprint/133014

Actions (login required)

View Item