Studi Pengaruh Treatment SiC Terhadap Morfologi Dan Sifat Mekanik Pada Komposit Hibrid Epoksi/Serat Karbon/SiC Untuk Aplikasi Material Anti Peluru (Body Armor).

Mayasari, Hesty Eka (2022) Studi Pengaruh Treatment SiC Terhadap Morfologi Dan Sifat Mekanik Pada Komposit Hibrid Epoksi/Serat Karbon/SiC Untuk Aplikasi Material Anti Peluru (Body Armor). Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6011201003-Master_Thesis.pdf Restricted to Repository staff only Download (4MB)

Abstract

Komposit polimer merupakan kandidat material tahan peluru dengan densitas yang rendah sehingga lebih nyaman saat digunakan. Penambahan bahan pengisi serat karbon dan silikon karbida (SiC) pada epoksi dapat menghasilkan komposit hibrid dengan sifat mekanik yang unggul. Perlakuan awal bahan pengisi dapat meningkatkan sifat mekanik komposit. Penelitian ini bertujuan untuk menganalisis pengaruh perlakuan kimia dan termal pada SiC terhadap morfologi dan sifat mekanik komposit epoksi/serat karbon/SiC untuk aplikasi material anti peluru. Perlakuan kimia dilakukan dengan perendaman SiC dalam larutan acetic anhydride (Ac2O) dengan konsentrasi 4,8,12,16% dan perlakuan termal dengan pemanasan awal SiC pada 500,600,700,800⁰C. Pembuatan komposit dilakukan dengan metode hand lay up. Perlakuan kimia dan termal tidak memberi pengaruh signifikan pada morfologi SiC. Perlakuan kimia dan termal meningkatkan kuat tarik dan kuat bending komposit. Perlakuan kimia meningkatkan kuat tarik serta kuat bending komposit hingga 84.9 MPa dan 65 MPa. Konsentrasi Ac2O yang semakin tinggi meningkatkan kuat tarik serta kuat bending komposit yang dapat diakibatkan karena adanya mekanisme interlocking. Perlakuan termal meningkatkan kuat tarik dan kuat bending komposit hingga 46.5 MPa dan 38.9 MPa. Pada pemanasan 500 ⁰C terjadi peningkatan kuat tarik dan kuat bending, kemudian terjadi penurunan pada pemanasan yang lebih tinggi akibat adanya lapisan oksidatif. Perlakuan kimia dengan 12 dan 16% Ac2O menghasilkan komposit epoksi/serat karbon/SiC yang sangat potensial untuk menjadi material anti peluru.
===================================================================================================================================
Polymer composite is a candidate for body armor materials with low density, making them more comfortable to use. The addition of carbon fiber and silicon carbide (SiC) fillers to the epoxy matrix can produce hybrid composites with superior mechanical properties. Pre-treatment of the filler material can improve the mechanical properties of the composite. This study aims to analyze the effect of chemical and thermal treatment on SiC on morphological and mechanical properties of epoxy/carbon fiber/SiC composites for the application of body armor materials. Chemical treatment are carried out by immersing SiC in a solution of acetic anhydride (Ac2O) with a concentration of 4,8,12.16% and thermal treatment with SiC preheating at 500,600,700,800⁰C. Composites are made using the hand lay up method. Chemical and thermal treatment had no significant effect on SiC morphology. Chemical and thermal treatment of SiC can produce epoxy/carbon fiber/SiC composites with good mechanical properties Chemical treatment increase the tensile and bending strength of the composite up to 84.9 MPa and 65 MPa. The higher Ac2O concentration, the higher tensile and bending strength because of interlocking mechanism. Thermal treatment of SiC increases the tensile and bending strength of composites up to 46.5 MPa and 38.9 MPa. The tensile and bending strength increase with preheating SiC at 500 ⁰C, but at higher preheating temperature, the tensile strength and bending strength decrease due to the presence of an oxidative layer. Chemical treatment with 12 and 16% Ac2O produce epoxy/carbon fiber/SiC composite that very potential to be a body armor material.

Item Type:	Thesis (Masters)
Additional Information:	RTMt 620.118 May s-1 2022
Uncontrolled Keywords:	Epoksi, serat karbon, silikon karbida, acetic anhydride, perlakuan awal, body armor. Epoxy, carbon fiber, silicon carbide, acetic anhydride, pretreatment, body armor.
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Chemical Engineering > 24101-(S2) Master Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	13 May 2026 02:29
Last Modified:	13 May 2026 02:43
URI:	http://repository.its.ac.id/id/eprint/133182