Analisis Pengaruh Perbandingan Komposisi Nitrogen Doping Dengan Karbon Aktif Pada Elektroda NAC/MNO2 Terhadap Morfologi Dan Performa Elektrokimia Superkapasitor.

Abyan, Demas Muhammad (2022) Analisis Pengaruh Perbandingan Komposisi Nitrogen Doping Dengan Karbon Aktif Pada Elektroda NAC/MNO2 Terhadap Morfologi Dan Performa Elektrokimia Superkapasitor. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000072-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (7MB)

Abstract

Perkembangan teknologi serta meningkatnya efek rumah kaca menuntut manusia untuk terus berinovasi. Salah satu yang menjadi menarik baru-baru ini adalah dalam bidang konversi energi. Mobil yang dulunya menggunakan bahan bakar fosil sekarang mulai berpindah menggunakan listrik. Penyimpanan energi listrik untuk kendaraan listrik salah satunya adalah dapat dengan menggunakan dukungan superkapasitor. Pada penelitian ini material yang digunakan adalah Nitrogen Activated Carbon (NAC) dan Manganese Dioxide (MnO2) dengan tujuan untuk menganalisis pengaruh nitrogen terhadap morfologi serta sifat elektrokimia NAC/MnO2. Metode yang digunakan pada sintesis ini adalah pirolisis yang diawali dengan proses aktivasi karbon dari limbah biomassa dengan KOH sebagai agen chemical activation yang divariasikan dengan polyaniline sebagai prekursor nitrogen dengan perbandingan komposisi AC: Polyaniline: KOH yang digunakan adalah sebagai berikut 1:0:3, 0,67:0,33:3, 0,5:0,5:3, 0,4:0,6:3 yang diberi nama NAC1, NAC2, dan NAC3. Kemudian dari hasil tersebut dilakukan pengujian XRD, FTIR, SEM untuk menganalisis morfologi kemudian CV untuk menganalisis performa elektrokimia. Didapati bahwa penambahan polyaniline sebagai dopan nitrogen, dapat menggeser puncak dari hasil XRD dan menambah BET surface area namun tidak berpengaruh terhadap morfologi. Dari perhitungan pengujian elektrokimia didapat nilai kapasitansi terbaik yaitu NAC3 yaitu 231,38 F/g pada scan rate 5 mV/s dengan tambahan elektrolit redox additive KI yang kemudian dihitung nilai energi density dan power density-nya yaitu sebesar 20,56 Wh/Kg dan 232,1 W/Kg.
===================================================================================================================================
Technological developments and the increasing greenhouse effect require humans to continue to innovate. One that has become of interest recently is in the field of energy conversion. Cars that used to use fossil fuels are now starting to switch to using electricity. One of the ways to store electrical energy for electric vehicles is to use supercapacitor support. In this study, the materials used were Nitrogen Activated Carbon (NAC) and Manganese Dioxide (MnO2) with the aim of analyzing the effect of nitrogen on the morphology and electrochemical properties of NAC/MnO2. The method used in this synthesis is pyrolysis which begins with the activation process of carbon from biomass waste with KOH as a chemical activation agent which is varied with polyaniline as nitrogen precursor with a ratio of AC: Polyaniline: KOH composition used is as follows 1:0:3, 0 ,67:0,33:3, 0,5:0,5:3, 0,4:0,6:3 which are named NAC1, NAC2, and NAC3. Then from these results, XRD, FTIR, SEM tests were carried out to analyze morphology and then CV to analyze electrochemical performance. It was found that the addition of polyaniline as nitrogen dopant could shift the peaks of the XRD results and increase the BET surface area but had no effect on morphology. From the calculation of the electrochemical test, the best capacitance value is NAC3, which is 231.38 F/g at a scan rate of 5 mV/s with the addition of redox additive KI electrolyte, which then calculates the energy density and power density values of 20.56 Wh/Kg and 232.1 W/Kg.

Item Type:	Thesis (Other)
Additional Information:	RSMt 621.312 429 Aby a-1 2022
Uncontrolled Keywords:	Doping, Karbon Aktif, Mangan Dioksida, Superkapasitor. Activated Carbon, Doping, Manganese Dioxide, Supercapacitorssi.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	18 May 2026 03:10
Last Modified:	18 May 2026 03:10
URI:	http://repository.its.ac.id/id/eprint/133211