Performa Perubahan Massa Dan Kuat Tekan Beton Geopolimer Berbasis High Calcium Fly Ash Akibat Pengaruh Paparan Sulfat

Azmi, Ahmad Daffa (2022) Performa Perubahan Massa Dan Kuat Tekan Beton Geopolimer Berbasis High Calcium Fly Ash Akibat Pengaruh Paparan Sulfat. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10111810010033-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (8MB) | Request a copy

Abstract

Lingkungan sulfat adalah salah satu keadaan yang sangat berpengaruh pada keawetan beton. Serangan sulfat dapat sering dijumpai di air laut, bawah tanah dan tumpukkan limbah kimia. Serangan sulfat pada beton mengakibatkan retak dan beton yang dapat mempengaruhi mutu beton. Oleh karena itu, dibutuhkan inovasi beton yang dapat menahan serangan sulfat. Beton geopolimer adalah terobosan baru yang bisa dikembangkan sebagai alternatif sebagai tanpa campuran semen portland. Bahan campuran beton geopolimer Fly Ash sendiri pada umumnya menggunakan fly ash tipe F dengan kadar CaO yang rendah, namun diindonesia keberadaan fly ash tipe C dengan kadar CaO yang tinggi sangat melimpah. Tingginya kadar kalsium membuat beton geopolimer menjadi keras dalam waktu yang singkat, dalam penelitian sebelumnya menggunakan sukrosa sebagai bahan tambah admixture dalam mengatasi masalah waktu pengerasan. Penelitian ini bertujuan untuk mengetahui pengaruh sulfat pada beton geopolimer berbasis fly ash tipe C serta menggunakan sukrosa sebagai superplastisizer. Beton geopolimer direndam dalam larutan natrium sulfat. Massa dan kuat tekan beton geopolimer akan ditinjau dipenelitian ini. Selain itu pH larutan natrium sulfat juga akan diuji untuk mengetahui perubahan nilai pH dari larutan. Penelitian ini menggunakan benda uji silinder berukuran 10 cm x 20 cm dengan metode pencampuran kering dan target kuat tekan sebesar 28 MPa sesuai SNI 2847 – 2019. Hasil penelitian kuat tekan beton pada usia 28 hari mencapai 38,25 MPa menunjukkan bahwa telah memenuhi standar SNI 2847-2019 untuk implementasi di lingkungan sulfat dengan klasifikasi S1, yaitu lebih dari 28 MPa. Hasil kuat tekan pada umur 84 hari dengan paparan natrium sulfat mendapatkan nilai kuat tekan 36,45 MPa dan nilai kuat tekan untuk Ambient Curing mendapatkan nilai kuat tekan 43,67 MPa. Nilai perubahan massa beton geopolimer mengalami peningkatan sebesar 0,338 persen. Sedangkan perubahan massa beton perawatan Ambient curing mengalami penurunan berat sebesar 0,224 persen. Nilai slump yang didapat berada pada rentang 150-230 mm sesuai syarat SNI 1972-2008. Penelitian jangka panjang diperlukan untuk mengevaluasi sulfat terhadap beton geopolimer berbasis fly ash tipe C.
==============================================================================================================================
The sulfate environment is one of the conditions that greatly affects the durability of concrete. Sulfate attack can often be found in seawater, underground and chemical waste piles. Sulfate attack on concrete causes cracks and concrete which can affect the quality of concrete. Therefore, it is necessary to innovate concrete that can withstand sulfate attack. Geopolymer concrete is a new breakthrough that can be developed as an alternative without a mixture of portland cement. Fly Ash geopolymer concrete mix materials generally use F type fly ash with low CaO content, but in Indonesia the presence of C type fly ash with high CaO content is very abundant. The high calcium content makes geopolymer concrete hard in a short time, in previous studies using sucrose as an admixture additive in overcoming the problem of hardening time. This study aims to determine the effect of sulfate on geopolymer concrete based on type C fly ash and using sucrose as a superplasticizer. Geopolymer concrete is immersed in a sodium sulfate solution. The mass and compressive strength of geopolymer concrete will be reviewed in this study. In addition, the pH of the sodium sulfate solution will also be tested to determine changes in the pH value of the solution. This study uses a cylindrical specimen measuring 10 cm x 20 cm with a dry mixing method and a target compressive strength of 28 MPa according to SNI 2847 – 2019. The results of the research that the compressive strength of concrete at the age of 28 days reached 38.25 MPa, indicating that it has met the SNI 2847-2019 standard for implementation in a sulfate environment with the S1 classification, which is more than 28 MPa. The results of the compressive strength at the age of 84 days with exposure to sodium sulfate got a compressive strength value of 36.45 MPa and the compressive strength value for Ambient Curing got a compressive strength value of 43.67 MPa. The change value of geopolymer concrete mass increased by 0.338 percent. Meanwhile, the change in the mass of ambient curing treated concrete experienced a weight loss of 0.224 percent. The slump value obtained is in the range of 150-230 mm according to the requirements of SNI 1972-2008. Long-term research is needed to evaluate sulfate against type C fly ash-based geopolymer concrete.Keywords:

Item Type:	Thesis (Diploma)
Additional Information:	RSIS 620.136 Azm p-1 2022
Uncontrolled Keywords:	Beton Geopolimer, high-calium fly ash, Sulfat. Geopolymer Concrete, high-calcium fly ash, Sulfate.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Faculty of Vocational > 22301-Civil Infrastructure Engineering (D4)
Depositing User:	Mr. Marsudiyana -
Date Deposited:	13 Jul 2026 03:26
Last Modified:	13 Jul 2026 03:26
URI:	http://repository.its.ac.id/id/eprint/134768

Actions (login required)

View Item