PEMANFAATAN ZEOLIT DAN SILIKA SEBAGAI MEMBRAN FILTRASI UNTUK MENURUNKAN TSS,COD DAN WARNA LIMBAH CAIR BATIK

PRAMITASARI, NOVEN (2016) PEMANFAATAN ZEOLIT DAN SILIKA SEBAGAI MEMBRAN FILTRASI UNTUK MENURUNKAN TSS,COD DAN WARNA LIMBAH CAIR BATIK. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
3314201027-Master_Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Salah satu penyebab pencemaran badan air adalah pembuangan limbah cair indusri yang tidak sesuai dengan baku mutu secara langsung ke badan air. Salah satu industri yang menghasilkan limbah cair adalah industri batik. Industri batik yang merupakan industri tekstil memiliki kadar total suspended solid (TSS), chemical oxygen demand (COD) dan warna yang memerlukan pengolahan sebelum dibuang ke badan air. Salah satu teknologi pengolahan adalah menggunakan membran filtrasi. Untuk memperkecil biaya pembuatan membran dan meningkatkan masa pakai membran filtrasi maka digunakan zeolit dan silika sebagai bahan pembuat membran. Variabel penelitian ini adalah perbandingan massa penambahan silika, kecepatan centrifuge pada pembuatan membran dan konsentrasi limbah cair batik yang akan diolah. Pengujian kinerja membran dilakukan dengan reaktor cross flow untuk meminimalkan biaya operasi sedangkan karakterisasi membran dilakukan dengan menggunakan uji scanning electron microscope (SEM), energy dispersif x-ray (EDX) dan kuat tarik. Analisa penelitian menggunakan data paremeter penelitian yaitu TSS, COD dan warna, nilai rejeksi dan nilai fluks membran. Nilai rejeksi TSS, COD dan warna pada membran dengan massa penambahan silika 3%, 600 RPM dan konsentrasi limbah 100% adalah 89,9 %; 72,86 % dan 92,68% sedangkan penurunan nilai fluks terkecil diperoleh pada membran dengan massa penambahan silika 3%, kecepatan centrifuge 600 rpm dan pengujian pada konsentrasi limbah cair batik 75% sebesar 1-7%. Membran dengan nilai rejeksi yang paling besar dan penurunan nilai fluks yang paling kecil adalah membran dengan massa penambahan silika 3% dan kecepatan centrifuge 600 rpm. ========== One of the causes of surface water pollution is industrial wastewater disposal directly into water bodies. One of the industries that produce wastewater is batik industry. Batik industry is the textile industry had higher levels of total suspended solid (TSS), chemical oxygen demand (COD) and colors that require treatment before being discharged into surface water. One such technology is membrane filtration. To minimize the cost of making the membrane and increase the lifetime of the membrane filtration then used zeolites and silica as the material for the membrane. The variables of this study is the mass of addition silica, centrifugation speed in the manufacture of the membrane and the concentration of batik wastewater. Testing the performance of the membrane is done with cross flow reactor to minimize operating costs while membrane characterization performed using scanning electron microscope (SEM), energy dispersif x-ray (EDX) test and tensile strength. Analysis of research studies using the data parameter is TSS, COD and color, rejection and flux value of membrane. Rejection value of TSS, COD and color on the membrane with a mass addition of silica 3%, 600 RPM and 100% effluent concentration is 89,9%; 72,86% and 92,68%, while the smallest decrease in the flux values obtained in the membrane with the addition of silica 3% mass, centrifugation speed of 600 rpm and testing on effluent concentration batik 75% of 1-7%. Membrane with a rejection of the greatest value and impairment of the smallest flux is membrane with a mass addition of 3% silica and centrifugation speed of 600 rpm.

Item Type: Thesis (Masters)
Uncontrolled Keywords: Membran, zeolit, silika, limbah dan cross flow, Membrane, zeolite, silica, wastewater and cross flow
Subjects: T Technology > TD Environmental technology. Sanitary engineering > TD646 Sewage--Purification
Divisions: Faculty of Civil Engineering and Planning > Environment Engineering > (S2) Master Theses
Depositing User: - Davi Wah
Date Deposited: 06 Jan 2017 04:27
Last Modified: 27 Dec 2018 03:41
URI: http://repository.its.ac.id/id/eprint/1362

Actions (login required)

View Item View Item