Analisis Pengaruh Penambahan Tio2 Pada Coating Anti-Bakterial Berbasis Resin Epoksi Minyak Kelapa Sawit

Rispo, Nathania Sabatina (2026) Analisis Pengaruh Penambahan Tio2 Pada Coating Anti-Bakterial Berbasis Resin Epoksi Minyak Kelapa Sawit. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011221115-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Indonesia merupakan produsen minyak kelapa sawit terbesar di dunia dengan kontribusi lebih dari 50% terhadap produksi global. Ketersediaan sumber daya yang melimpah ini membuka peluang besar untuk pemanfaatan minyak kelapa sawit tidak hanya sebagai komoditas pangan, tetapi juga sebagai bahan baku kimia terbarukan pada industri material. Salah satu pemanfaatannya adalah konversi minyak kelapa sawit melalui proses epoksidasi menjadi resin epoksi yang berpotensi digunakan sebagai matriks polimer ramah lingkungan. Resin epoksi disintesis melalui epoksidasi CPO menggunakan asam asetat dan hidrogen peroksida. TiO₂ difungsionalisasi dengan GPTMS 3 wt% dari massa TiO₂ melalui sonikasi dan pengeringan. Formulasi coating dibuat dengan mendispersikan TiO₂ dan GPTMS ke dalam resin, ditambahkan hardener poliamina kemudian diaplikasikan pada SS AISI 304 menggunakan kuas dan curing 24 jam pada 25°C. Karakterisasi dilakukan menggunakan FTIR, XRD, SEM/EDX, serta uji antibakteri dan uji adhesi pull-off. Hasil pengujian aktivitas antibakteri diperoleh pada EPO 7:3 + TiO₂ 5 wt% (D2), menunjukkan adanya kadar optimum TiO₂ untuk kinerja antibakteri. Pada pengujian adhesi, hasil penelitian dengan nilai terbaik berada pada EPO 7:3 + TiO₂ 7 wt% (D3) dengan kekuatan pull-off 2,19 ± 0,72 MPa. FTIR mengonfirmasi keberadaan pita karakteristik sistem coating dan kontribusi TiO₂, termasuk pita Ti–O–Ti pada 448 cm⁻¹, sementara SEM–EDX menunjukkan sebaran unsur Ti yang merata pada permukaan dengan partikel Ti terukur 17,32 wt% pada area analisis.
=====================================================================================================================================
Indonesia is the largest palm oil producer in the world with a contribution of more than 50% to global production. The availability of this abundant resource opens up great opportunities for the utilization of palm oil not only as a food commodity, but also as a renewable chemical raw material in industrial materials. One of its uses is the conversion of palm oil through an epoxidation process into epoxy resin which has the potential to be used as an environmentally friendly polymer matrix. Epoxy resin is synthesized through the epoxidation of CPO using acetic acid and hydrogen peroxide. TiO₂ is functionalized with GPTMS 3 wt% of the TiO₂ mass through sonication and drying. The coating formulation is made by dispersing TiO₂ and GPTMS into the resin, adding polyamine hardener then applied to SS AISI 304 using a brush and curing for 24 hours at 25°C. Characterization is carried out using FTIR, XRD, SEM/EDX, as well as antibacterial and pull-off adhesion tests. The results of the antibacterial activity test obtained on EPO 7:3 + TiO₂ 5 wt% (D2), indicate the optimal TiO₂ content for antibacterial performance. In the adhesion test, the research results with the best value were on EPO 7:3 + TiO₂ 7 wt% (D3) with a pull-off strength of 2.19 ± 0.72 MPa. FTIR confirmed the presence of characteristic bands of the coating system and the contribution of TiO₂, including the Ti–O–Ti band at 448 cm⁻¹, while SEM–EDX showed an even distribution of Ti elements on the surface with Ti particles measuring 17.32 wt% in the analysis area.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Coating, Antibakteri, TiO2, Resin Epoksi, Minyak Kelapa Sawit
Subjects:	R Medicine > RZ Other systems of medicine
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Nathania Sabatina Rispo
Date Deposited:	23 Jul 2026 15:45
Last Modified:	23 Jul 2026 15:45
URI:	http://repository.its.ac.id/id/eprint/136994

Actions (login required)

View Item