Analisis Recovery Nikel dan Kobalt dari Converter Slag melalui Variasi Intensitas Magnet dan Ukuran Partikel pada Drum Magnetic Separator

Kartikasari, Cindy Putri (2026) Analisis Recovery Nikel dan Kobalt dari Converter Slag melalui Variasi Intensitas Magnet dan Ukuran Partikel pada Drum Magnetic Separator. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011221004-Undergradute_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Indonesia merupakan negara yang memiliki cadangan nikel terbesar di dunia yang berperan penting dalam mendukung transisi energi khususnya untuk kebutuhan baterai kendaraan listrik dan system penyimpanan energi. Proses pengolahan nikel laterit dilakukan melalui metode Rotary Kiln – Electric Furnace (RKEF) yang menghasilkan produk samping berupa slag dalam converter yang masih mengandung logam berharga seperti nikel dan kobalt dalam bentuk oksida maupun sulfida kompleks. Penelitian ini bertujuan untuk menganalisis pemulihan nikel dan kobalt dari converter slag menggunakan drum magnetic separator dengan adanya pengaruh variasi ukuran partikel dan intensitas magnet terhadap nilai recovery dan kadar yang dihasilkan. Variasi ukuran partikel yang digunakan adalah (-) 250, (-) 125, (-) 75,(-) 50, dan (-) 38 μm dengan hasil optimal didapatkan pada variasi ukuran partikel (-) 250 dengan nilai recovery mencapai 99,6% dan kadar nikel dan kobalt meningkat dari raw yang awalnya 2,6% dan 0,28% menjadi 3,7% dan 0,3%. Variasi intensitas magnet yang digunakan adalah 5.000, 10.000, dan 14.000 gauss dengan hasil optimal didapatkan pada variasi intensitas14.000 gauss dengan nilai recovery mencapai 99,5% serta kadar nikel dan kobalt megalami peningkatan dari raw yaitu 0,67% dan 0,213% menjadi 0,71% dan 0,219%. Hasil XRD menunjukkan bahwa fasa yang terkandung dalam converter slag adalah fayalite (Fe2SiO4) sebagai fasa utama dan beberapa fasa minor seperti pentlandite ((Fe,Ni)9S8), quartz (SiO2), dan magnetite (Fe3O4). Proses produksi pengolahan slag diawali dari crushing hingga klasifikasi ukuran sebelum masuk ke magnetic separator. Secara ekonomi, variasi (-) 125 μm di 14.000gauss adalah yang paling menguntungkan dengan nilai profit $MM1,4/year dan payback period dalam waktu singkat yaitu 7 tahun.
=====================================================================================================================================
Indonesia is a country with the largest nickel reserves in the world and plays an important role in supporting the energy transition, particularly for electric vehicle batteries and energystorage systems. Laterite nickel processing is carried out using the Rotary Kiln–Electric Furnace (RKEF) method, which produces slag as a by-product in the converter that still contains valuable metals such as nickel and cobalt in the form of oxides and complex sulfides. This study aims to analyze the recovery of nickel and cobalt from converter slag using a drum magnetic separator by evaluating the effect of particle size variation and magnetic intensity on therecovery and grade obtained. The particle size variations investigated were (-) 250, (-) 125, (-)75, (-) 50, and (-) 30 μm. The optimum result was obtained at the (-) 250 μm particle size, achieving a nickel recovery of 99,6%, while the nickel and cobalt grades increased from 2,6%and 0,28% in the raw material to 3,7% and 0,30%, respectively. The magnetic field intensities applied were 5.000, 10.000, and 14.000 Gauss. The optimum magnetic intensity was 14.000gauss, resulting 99,5% nickel recovery, with the nickel and cobalt grades increasing from 0,67%and 0,213% in the raw material to 0,71% and 0,219%, respectively. XRD analysis identified fayalite (Fe₂SiO₄) as the dominant phase, accompanied by minor phases including pentlandite((Fe,Ni)₉S₈), quartz (SiO₂), and magnetite (Fe₃O₄). The proposed processing route consists of crushing, particle size classification, and magnetic separation. Economic evaluation indicated that the (-) 125 μm particle size and 14.000 gauss provided the highest economic benefit, yielding a gross profit of $MM1,4/year with a payback period of 7 years.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Converter Slag, Drum Magnetic Separator, Kobalt, Nikel, Recovery Cobalt, Converter Slag, Drum Magnetic Separator, Nickel, Recovery
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN799.N6 Nickel--Metallurgy
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Cindy Putri Kartikasari
Date Deposited:	24 Jul 2026 03:04
Last Modified:	24 Jul 2026 08:35
URI:	http://repository.its.ac.id/id/eprint/137016

Actions (login required)

View Item