Analisis Pengaruh Dari Desain Lance Dan Waktu Degassing Menggunakan Gas Ar Terhadap Sifat Mekanik Dan Struktur Mikro Pada Aluminium 6061

Irawan, Victorio (2026) Analisis Pengaruh Dari Desain Lance Dan Waktu Degassing Menggunakan Gas Ar Terhadap Sifat Mekanik Dan Struktur Mikro Pada Aluminium 6061. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011221154-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (9MB)

Abstract

Aluminium 6061 merupakan jenis paduan Al-Mg-Si yang umum digunakan di bidang konstruksi, transportasi, serta industri. Dengan memanfaatkan sifatnya yang ringan dan tahan korosi. Dalam proses pengecoran hidrogen yang terlarut di aluminium cair dapat menjadi tantangan tersendiri. Hidrogen terlarut tersebut akan meninggalkan aluminium menjadi porosistas. Dengan proses degassing dapat dimanfaatkan kemampuian suatu gas untuk mengurangi kandungan hidrogen yang telah terlarut. Hal tersebut dapat dipengaruhi oleh faktor desain lance serta waktu prosesnya. Penelitian ini bertujuan dalam menganalisis pengaruh Lance A dan B dengan variasi waktu 4, 8, dan 10 menit terhadap sifat mekanik dan strukutr mikro aluminium 6061. Terdapat beberapa karakterisasi yang dilakukan seperti OES untuk menunjukkan persentase komposisi unsur, SEM untuk melihat morfologi patahan. Metalografi untuk melihat struktur mikro, dan XRD untuk melihat puncak dari kristal yang terdapat. Hasil OES menunjukkan bahwa komposisi material berada dalam rentang aluminium 6061, sedangkan hasil XRD menunjukkan bahwa fasa utama seluruh spesimen adalah α-Al. Pengamatan metalografi dan SEM memperlihatkan bahwa desain lance dan waktu degassing memengaruhi ukuran serta penyebaran porositas. Pada Lance A, porositas terendah diperoleh pada waktu 10 menit sebesar 0,74%, sedangkan pada Lance B porositas terendah diperoleh pada waktu 4 menit sebesar 0,48%. Nilai ultimate tensile strength tertinggi diperoleh pada Lance A selama 4 menit sebesar 184,92 MPa dengan elongasi 38,41%, sedangkan Lance B selama 4 menit menghasilkan UTS sebesar 182,60 MPa. Nilai kekerasan tertinggi diperoleh pada Lance B selama 10 menit sebesar 68,30 HV. Secara keseluruhan, kombinasi Lance B dengan waktu degassing 4 menit menghasilkan kondisi paling optimum karena memberikan porositas terendah dengan kekuatan tarik yang tetap tinggi.
==============================================================================================================================
Aluminum 6061 is a type of Al-Mg-Si alloy commonly used in the construction, transportation, and industrial sectors, taking advantage of its lightweight and corrosion-resistant properties. During the casting process, dissolved hydrogen in molten aluminum can pose a unique challenge. This dissolved hydrogen causes porosity in the aluminum. The degassing process utilizes the ability of a gas to reduce the dissolved hydrogen content. This process is influenced by the lance design and the duration of the process. This study aims to analyze the effect of Lance A and B, with process times of 4, 8, and 10 minutes, on the mechanical properties and microstructure of 6061 aluminum. Several characterization methods were employed, including OES to determine elemental composition percentages, SEM to examine fracture morphology, metallography to analyze the microstructure, and XRD to identify crystal peaks. The OES results showed that the material composition fell within the range of 6061 aluminum, while the XRD results indicated that the primary phase in all specimens was α-Al. Metallographic and SEM observations revealed that the lance design and degassing time influenced the size and distribution of porosity. For Lance A, the lowest porosity was obtained at 10 minutes, at 0.74%, while for Lance B, the lowest porosity was obtained at 4 minutes, at 0.48%. The highest ultimate tensile strength (UTS) was obtained for Lance A at 4 minutes, at 184.92 MPa with an elongation of 38.41%, while Lance B at 4 minutes yielded an UTS of 182.60 MPa. The highest hardness value was obtained for Lance B at 10 minutes, at 68.30 HV. Overall, the combination of Lance B with a 4-minute degassing time produced the most optimal conditions because it provided the lowest porosity while maintaining high tensile strength.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Aluminium 6061, Degassing, Desain Lance, Kekuatan Mekanis, Aluminium 6061, Degassing, Lance Design, Mechanical Strength
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL671.6. Materials--Fatigue. T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy T Technology > TS Manufactures
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering
Depositing User:	Victorio Irawan
Date Deposited:	27 Jul 2026 03:21
Last Modified:	27 Jul 2026 03:21
URI:	http://repository.its.ac.id/id/eprint/137841

Actions (login required)

View Item