PREPARASI LAPISAN TIPIS ZnO DENGAN METODE ELEKTRODEPOSISI UNTUK APLIKASI DYE-SENSITIZED SOLAR CELL (DSSC)

MOHAMMAD, ROHMAD W. and FARIS, SALMAN (2015) PREPARASI LAPISAN TIPIS ZnO DENGAN METODE ELEKTRODEPOSISI UNTUK APLIKASI DYE-SENSITIZED SOLAR CELL (DSSC). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
2310100027-2310100141-Undergraduate_theses.pdf - Published Version
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mempelajari dan mengevaluasi pengaruh dari potensial yang diaplikasikan saat elektrodeposisi terhadap morfologi dan karakteristik lapisan ZnO yang terbentuk, serta mempelajari pengaruh pewarnaan dengan antosianin dari ekstrak kulit terong terhadap sifat photovoltaic. Proses elektrodeposisi dilakukan dengan 3 elektroda yaitu, elektroda kerja berupa Cu dan ITO Glass, elektroda lawan berupa platina dan elektroda pembanding berupa Ag/AgCl. Media elektrolit yang digunakan berupa larutan campuran 5 mM ZnCl2 dan 0,1 M KCl dalam air demin, dengan volume total 600 ml. Larutan diinjeksi dengan oksigen hingga mencapai DO 16,5 mg/L, selanjutnya dilakukan elektrodeposisi selama 30 menit. Elektrodeposisi dilakukan pada berbagai potensial yaitu -0,5V; -0,75V; -1V; -1,25V dan -1,5V vs Ag/AgCl. Kemudian nilai konditivitas dari elektroda kerja diamati secara Chrono Amperometry dengan menggunakan Autolab 302N, Metrohm. Selanjutnya dianalisa reaksi yang terjadi pada elektrolit dengan Cyclic Voltemmetry. Lalu untuk hasil lapisan ZnO yang telah terbentuk diamati dengan Scanning Electron Microscopy (SEM). Besar hambatan listrik dengan metode uji resistivity 4 probe. Hasil penelitian menunjukkan perbedaan potensial saat elektrodeposisi memberikan pengaruh terhadap proses pelapisan dan morfologi dari ZnO. Pada potensial rendah, proses pelapisan akan berlangsung lambat menghasilkan ZnO yang porous dan merata. Semakin tinggi potesial yang diaplikasikan maka proses pelapisan akan semakin cepat dan ZnO yang terbentuk akan semakin tebal. Hasil lapisan yang memiliki nilai resistansi terkecil adalah ZnO pada potensial -1,5V vs Ag/AgCl. ============================================================ The purposes of this research are to study and to evaluate the effect of applied potential of electrodeposition to morphology and characteristic of ZnO layer formed, also effect of anthocyanin dye-coloring from extract of purple eggplant peels to photovoltaic characteristic. Electrodeposition carried out with 3 electrodes which, working electrode was ITO Glass, Counter electrode was platinum, and reference electrode was Ag/AgCl. Electrolyte media containing 5 mM ZnCl2 and 0,1 M KCl in demineralized water, with total volume 600 ml. Electrolyte injected with oxygen until dissolved oxygen value reach 16,5 mg/L, electrodeposition was conducted for 30 minutes. Electrodeposition carried out in several potentials, -0,5V; -0,75V; -1V; -1,25V and -1,5V vs Ag/AgCl. The conductivity of working electrode can be analyzed with chronoamperometry method with Autolab 302N, Metrohm. The reaction of electrolyte can be analyzed with Cyclic Voltammetry. Morphology of ZnO layer formed was observed with Scanning Electron Microscopy (SEM). The amount of electrical resistance ware analyzed with 4 probe resistivity method. The result shows that the applied potential of electrode have an effect on coating process and morphology of ZnO layer formed. On low potential, coating process was slow which formed porous and homogeny ZnO layer. More higher potential applied, the ZnO coating process become more faster and the layer become thicker. The layer which have lowest resistance value was ZnO formed on potential -1,5V vs Ag/AgCl.

Item Type: Thesis (Undergraduate)
Additional Information: RSK 661.808 Moh p
Uncontrolled Keywords: Elektrodeposisi, lapisan ZnO, Dissolved Oxygen, ITO Glass
Subjects: T Technology > TP Chemical technology > TP255 Electrochemistry, Industrial.
Divisions: Faculty of Industrial Technology > Chemical Engineering > (S1) Undergraduate Theses
Depositing User: Mrs Anis Wulandari
Date Deposited: 09 Jan 2017 02:55
Last Modified: 09 Jan 2017 02:55
URI: http://repository.its.ac.id/id/eprint/1389

Actions (login required)

View Item View Item