Analisis Pengaruh Variasi Tinggi Piramida Microwave Absorber Berbahan Dielektrik Berbasis Selulosa Untuk Aplikasi Anechoic Chamber

Setiyowati, Devi Sri Setiyowati (2026) Analisis Pengaruh Variasi Tinggi Piramida Microwave Absorber Berbahan Dielektrik Berbasis Selulosa Untuk Aplikasi Anechoic Chamber. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001221064_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Piramida Microwave Absorber (PMA) merupakan struktur penyerap gelombang elektromagnetik yang banyak digunakan pada anechoic chamber untuk mengurangi refleksi gelombang. Kinerja piramida dipengaruhi oleh dimensi geometrinya sehingga diperlukan kajian mengenai pengaruh variasi tinggi piramida terhadap karakteristik penyerapan gelombang elektromagnetik. Penelitian ini bertujuan untuk menganalisis pengaruh variasi tinggi piramida berbahan dielektrik berbasis selulosa terhadap karakteristik penyerapan gelombang elektromagnetik berdasarkan parameter transmisi (S12) dan absorbansi relatif. Penelitian ini menggunakan metode eksperimen dengan pengukuran parameter S12 menggunakan Vector Network Analyzer (VNA) melalui metode free-space reflection pada rentang frekuensi 0,3-18 GHz. Sampel yang diuji terdiri atas dua variasi piramida berbahan dielektrik berbasis selulosa dengan ukuran alas tetap 7 × 7 cm dan tinggi 18 cm serta 22 cm, menggunakan pelat aluminium sebagai referensi dan pelat aluminium yang dilapisi bahan dielektrik berbasis selulosa sebagai pembanding. Data hasil pengukuran S12 diolah untuk memperoleh nilai reflection loss dan absorbansi relatif, kemudian dianalisis pada UHF-S Band, C Band, X Band, dan Ku Band menggunakan dua indikator, yaitu rata-rata absorbansi relatif efektif dan jumlah titik frekuensi dengan nilai absorbansi relatif ≥ 50%. Hasil penelitian menunjukkan bahwa variasi tinggi piramida memengaruhi karakteristik penyerapan gelombang elektromagnetik pada setiap rentang frekuensi. Piramida dengan tinggi 18 cm menghasilkan rata-rata absorbansi relatif efektif tertinggi sebesar 92,80% pada UHF-S Band, 75,20% pada C Band, dan 76,35% pada X Band, sedangkan piramida dengan tinggi 22 cm menghasilkan rata-rata absorbansi relatif efektif tertinggi sebesar 79,86% pada Ku Band. Evaluasi menggunakan dua indikator menunjukkan bahwa tidak terdapat satu konfigurasi piramida yang secara konsisten memberikan karakteristik penyerapan terbaik pada seluruh rentang frekuensi. Hasil tersebut menunjukkan bahwa pengaruh variasi tinggi piramida terhadap karakteristik penyerapan gelombang elektromagnetik bersifat frequency dependent, sehingga pemilihan tinggi piramida perlu disesuaikan dengan rentang frekuensi aplikasi yang menjadi target penggunaan.
=========================================================================================================================================
Pyramidal Microwave Absorbers (PMAs) are electromagnetic wave-absorbing structures widely used in anechoic chambers to reduce wave reflections. The performance of a PMA is influenced by its geometric dimensions; therefore, investigating the effect of pyramid height variation on electromagnetic wave absorption characteristics is essential. This study aims to analyze the effect of variations in the height of cellulose-based dielectric pyramids on electromagnetic wave absorption characteristics based on the transmission parameter (S12) and relative absorbance. An experimental method was employed by measuring the S12 parameter using a Vector Network Analyzer (VNA) through the free-space reflection method over a frequency range of 0.3-18 GHz. The tested samples consisted of two cellulose-based dielectric pyramids with a constant base dimension of 7 × 7 cm and heights of 18 cm and 22 cm. An aluminum plate was used as the reference, while an aluminum plate covered with a cellulose-based dielectric material served as the comparison sample. The measured S12 data were processed to obtain the reflection loss and relative absorbance values, which were then analyzed in the UHF-S Band, C Band, X Band, and Ku Band using two indicators, namely the average effective relative absorbance and the number of frequency points with relative absorbance values of ≥ 50%. The results indicate that variations in pyramid height affect the electromagnetic wave absorption characteristics across different frequency ranges. The 18 cm pyramid exhibited the highest average effective relative absorbance of 92.80% in the UHF-S Band, 75.20% in the C Band, and 76.35% in the X Band, whereas the 22 cm pyramid achieved the highest average effective relative absorbance of 79.86% in the Ku Band. Evaluation using the two indicators revealed that no single pyramid configuration consistently provided the best absorption characteristics over the entire frequency range. These findings indicate that the effect of pyramid height variation on electromagnetic wave absorption characteristics is frequency-dependent, suggesting that the selection of pyramid height should be tailored to the intended application frequency range.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Absorbansi, Anechoic Chamber, Gelombang Elektromagnetik, Piramida Vector Network Anlyzer (VNA), Absorbance, Anechoic chamber, Electromagnetic waves, Pyramid, Vector Network Analyzer (VNA).
Subjects:	Q Science Q Science > QC Physics Q Science > QC Physics > QC162 Adsorption and absorption Q Science > QC Physics > QC585 Dielectrics Q Science > QC Physics > QC631.D29 Electrodynamics.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Devi Sri Setiyowati
Date Deposited:	29 Jul 2026 03:01
Last Modified:	29 Jul 2026 03:01
URI:	http://repository.its.ac.id/id/eprint/139408

Actions (login required)

View Item