AKTIVASI KARBON BERTEMPLAT ZEOLIT-Y DENGAN KOH UNTUK PENINGKATAN KAPASITAS ADSORPSI GAS CO2

SUSANTI, INDRI (2016) AKTIVASI KARBON BERTEMPLAT ZEOLIT-Y DENGAN KOH UNTUK PENINGKATAN KAPASITAS ADSORPSI GAS CO2. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1412100077-Undergraduate_theses.pdf]
Preview
Text
1412100077-Undergraduate_theses.pdf

Download (2MB) | Preview

Abstract

Penelitian ini bertujuan mengaktivasi karbon tertemplat
zeolit-Y dengan KOH untuk meningkatkan kapasitas adsorpsi gas
CO2. Karbon tertemplat zeolit-Y disintesis dengan metode
impregnasi disertai dengan karbonisasi. Proses aktivasi dilakukan
pada variasi rasio KOH(g)/KTZ-Y(g) = 0,5; 1; 1,5 dan 2
bertujuan untuk mendapatkan kapasitas adsorpsi gas CO2 yang
optimum. Aktivasi dilakukan melalui pemanasan KTZ-Y yang
telah diimpregnasi dengan KOH pada suhu 800°C selama 1 jam
dan pencucian untuk menghilangkan garam anorganik. KTZ-Y
sebelum dan setelah aktivasi dikarakterisasi dengan XRD, IR, dan
SEM. Uji kapasitas adsorpsi gas CO2 dilakukan dengan metode
gravimetri. Hasil yang diperoleh menunjukkan aktivasi KTZ-Y
dengan KOH dapat meningkatkan kapasitas adsorpsi gas CO2.
Kapasitas adsorpsi gas CO2 pada KTZ-Y sebelum aktivasi 1,07
%berat dan setelah aktivasi KOH meningkat hingga 2,72 %berat
pada rasio KOH(g)/ KTZ-Y(g) sebesar 1,5.

============================================================

This research aims to activate zeolite-Y templated carbon
with KOH for increasing CO2 adsorption capacity. Zeolite-Y
templated carbon was synthesized via impregnation method by
carbonization. Activation process was conducted at variation
weight ratio of KOH(g)/KTZ-Y(g) 0.5; 1; 1.5 and 2 in order to
obtain optimum of CO2 adsorption capacity. The activation was
performed by heating of impregnated KTZ-Y with KOH at 800°C
for 1 hour followed by acid washing to remove inorganic salt.
KTZ-Y before and after activation were characterized by XRD,
IR and SEM. The CO2 adsorption capacity was determined by
gravimetric method. The result show that activation of KTZ-Y
with KOH increased CO2 adsorption capacity. CO2 adsorption
capacity enhanced from 1.07% (wt) to 2.72% (wt) for zeolite-Y
template carbon after activation with KOH at weight ratio of
KOH(g)/ KTZ-Y(g) 1.5.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 549.68 Sus a
Uncontrolled Keywords: karbon tertemplat zeolit-Y, aktivasi, KOH, kapasitas adsorpsi gas CO2.
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Anis Wulandari
Date Deposited: 09 Jan 2017 03:58
Last Modified: 17 May 2024 07:36
URI: http://repository.its.ac.id/id/eprint/1398

Actions (login required)

View Item View Item