Sintesis Komposit WO3/MIL-125(Ti)/UiO-66 Berbasis Pasir Zirkon sebagai Fotokatalis untuk Produksi Metil Ester dari Asam Oleat Melalui Esterifikasi Fotokatalitik

Putri, Aulia Malihah (2026) Sintesis Komposit WO3/MIL-125(Ti)/UiO-66 Berbasis Pasir Zirkon sebagai Fotokatalis untuk Produksi Metil Ester dari Asam Oleat Melalui Esterifikasi Fotokatalitik. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004221134-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (9MB) | Request a copy

Abstract

Peningkatan kebutuhan energi dan emisi CO₂ akibat penggunaan bahan bakar fosil mendorong pengembangan biodiesel sebagai energi terbarukan. Metode esterifikasi fotokatalitik menawarkan proses yang lebih efisien melalui pemanfaatan energi cahaya sebagai sumber aktivasi reaksi. Penelitian ini bertujuan untuk mensintesis komposit WO₃/MIL-125(Ti)/UiO-66 berbasis pasir zirkon sebagai fotokatalis untuk produksi metil ester dari asam oleat. Komposit WO₃/MIL-125(Ti)/UiO-66 berbasis pasir zirkon disintesis melalui metode solvotermal dan impregnasi basah, kemudian dikarakterisasi menggunakan XRD, FTIR, XRF, SEM-EDX, adsorpsi-desorpsi N₂, dan UV-Vis DRS. Variasi komposisi WO3 yang digunakan adalah 3, 4, dan 5 wt% terhadap MIL-125(Ti)/UiO-66. Aktivitas esterifikasi fotokatalitik dievaluasi melalui optimasi pengaruh massa katalis, variasi komposit, rasio molar asam oleat terhadap metanol, suhu reaksi, dan waktu reaksi reaksi. Kinerja fotokatalis dianalisis berdasarkan nilai konversi asam lemak bebas (FFA) dan selektivitas metil ester yang diperoleh dari analisis titrasi dan uji GC-MS. Hasil pengujian menunjukkan bahwa komposit 10% WO₃/MIL-125(Ti)/UiO-66 memiliki aktivitas fotokatalitik yang baik dalam reaksi esterifikasi asam oleat menjadi metil ester. Komposit 10WMU menunjukkan kinerja terbaik dengan konversi FFA sebesar 78,34% dan selektivitas metil ester sebesar 27,22 pada waktu reaksi 2 jam, serta konversi FFA sebesar 57,54% dan selektivitas metil ester sebesar 34,08% pada waktu 3 jam. Kondisi reaksi optimum diperoleh pada massa katalis 3 wt%, rasio molar asam oleat 1:5, dan suhu 60-65 °C. Hasil penelitian menujukkan bahwa komposit WMU memiliki aktivitas fotokatalitik yang baik dalm reaksi esterifikasi asam oleat menjadi metil ester, sehingga berpotensi menjadi material fotokatalis yang efisien untuk dikembangkan sebagai fotokatalis heterogen dalam aplikkasi produksi metil ester melalaui proses esterifikasi.
=======================================================================================================================================
The increasing energy demand and CO₂ emissions due to the use of fossil fuels encourage the development of biodiesel as a renewable energy. The photocatalytic esterification method offers a more efficient process by utilizing light energy as a reaction activation source. This study aims to synthesize a zircon sand-based WO₃/MIL-125(Ti)/UiO-66 composite as a photocatalyst for the production of methyl esters from oleic acid. The zircon sand-based WO₃/MIL-125(Ti)/UiO-66 composite was synthesized through solvothermal and wet impregnation methods, then characterized using XRD, FTIR, XRF, SEM-EDX, N₂ adsorption-desorption, and UV-Vis DRS. The variations of WO₃ composition used were 3, 4, and 5 wt% of MIL-125(Ti)/UiO-66. The photocatalytic esterification activity was evaluated by optimizing the effect of catalyst mass, composite variations, oleic acid to methanol molar ratio, reaction temperature, and reaction time. The photocatalyst performance was analyzed based on the free fatty acid (FFA) conversion value and methyl ester selectivity obtained from titration analysis and GC-MS test. The test results showed that the 10% WO₃/MIL-125(Ti)/UiO-66 composite had good photocatalytic activity in the esterification reaction of oleic acid to methyl ester. The 10WMU composite showed the best performance with an FFA conversion of 78.34% and a methyl ester selectivity of 27.22 at a reaction time of 2 hours, and an FFA conversion of 57.54% and a methyl ester selectivity of 34.08% at a reaction time of 3 hours. The optimum reaction conditions were obtained at a catalyst mass of 3 wt%, an oleic acid molar ratio of 1:5, and a temperature of 60-65 °C. The research results show that the WMU composite exhibits good photocatalytic activity in the esterification reaction of oleic acid to methyl ester, thus potentially becoming an efficient photocatalyst material for development as a heterogeneous photocatalyst for methyl ester production through the esterification process.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Asam Oleat, Esterifikasi, Fotokatalitik, Komposit WO₃/MIL-125(Ti)/UiO-66, Metil ester, Esterification, Methyl ester, Oleic Acid, Photocatalytic, WO₃/MIL-125(Ti)/UiO-66 Composite.
Subjects:	Q Science Q Science > QD Chemistry Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Aulia Malihah Putri
Date Deposited:	04 Aug 2026 03:44
Last Modified:	04 Aug 2026 03:44
URI:	http://repository.its.ac.id/id/eprint/141433