Pengaruh Ph Dan Jenis Agen Presipitasi Terhadap Presipitasi Logam Tanah Jarang Dari Larutan Hasil Fusi Alkali Dan Pelindian Asam Sulfat Terak Timah

Choirurrizal, El Fatih Hafidz Choirurrizal (2026) Pengaruh Ph Dan Jenis Agen Presipitasi Terhadap Presipitasi Logam Tanah Jarang Dari Larutan Hasil Fusi Alkali Dan Pelindian Asam Sulfat Terak Timah. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011221049-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (8MB) | Request a copy

Abstract

Logam tanah jarang atau rare earth elements (REE) merupakan kelompok unsur strategis yang banyak digunakan dalam industri elektronik, magnet permanen, kendaraan listrik, dan teknologi energi terbarukan. Salah satu sumber sekunder REE yang berpotensi dikembangkan di Indonesia adalah terak timah. Namun, rendahnya kadar REE serta keberadaan berbagai unsur pengotor menyebabkan proses pengambilan dan pemisahannya memerlukan tahapan pengolahan yang sesuai. Penelitian ini bertujuan menganalisis pengaruh pH dan jenis agen presipitasi terhadap perilaku presipitasi serta komposisi endapan REE dari larutan hasil pengolahan terak timah. Terak timah terlebih dahulu diproses melalui fusi alkali menggunakan NaOH, dilanjutkan dengan water leaching dan pelindian menggunakan larutan H2SO4 untuk memindahkan REE ke dalam fase larutan. Filtrat hasil pelindian kemudian dipresipitasi menggunakan NH4OH dan Na2CO3 pada variasi pH 6, 7, dan 8. Larutan sebelum dan sesudah presipitasi dianalisis untuk mengevaluasi perpindahan unsur dari fase cair, sedangkan endapan dikarakterisasi untuk mengetahui komposisi unsur REE dan pengotor yang ikut terpresipitasi. Hasil penelitian menunjukkan bahwa pH dan jenis agen presipitasi memengaruhi jumlah serta komposisi unsur yang berpindah dari larutan ke fase padat. Peningkatan pH secara umum meningkatkan pembentukan endapan akibat meningkatnya ketersediaan ion hidroksida dan karbonat. Akan tetapi, presipitasi yang berlangsung tidak bersifat selektif terhadap salah satu unsur karena beberapa unsur REE lainnya turut terpresipitasi pada kondisi yang sama. Selain itu, unsur pengotor seperti Si, Ca, Ti, dan Zr juga ditemukan dalam endapan, yang menunjukkan terjadinya kopresipitasi dan terbawanya komponen matriks selama proses. Dengan demikian, proses yang dilakukan lebih tepat dinyatakan sebagai presipitasi bersama REE daripada pemisahan selektif suatu unsur REE. Pengaturan pH dan pemilihan agen presipitasi tetap berperan penting dalam mengendalikan perolehan dan komposisi endapan REE, tetapi diperlukan proses pemurnian lanjutan untuk memperoleh unsur REE individual dengan selektivitas yang lebih tinggi.
===================================================================================================================================
Rare earth elements (REE) are a group of strategic elements widely used in the electronics industry, permanent magnets, electric vehicles, and renewable energy technologies. One potential secondary source of REE in Indonesia is tin slag. However, the low REE content and the presence of various impurities require appropriate extraction and separation processes. This study aims to analyze the effects of pH and precipitating agent type on the precipitation behavior and composition of REE precipitates obtained from tin slag processing solutions. Tin slag was first processed through alkali fusion using NaOH, followed by water leaching and acid leaching with H₂SO₄ solution to transfer the REEs into the aqueous phase. The resulting leachate was then precipitated using NH₄OH and Na₂CO₃ at pH values of 6, 7, and 8. Solutions before and after precipitation were analyzed to evaluate the transfer of elements from the liquid phase, while the precipitates were characterized to determine the composition of REE elements and co-precipitated impurities. The results show that both pH and precipitating agent type influence the amount and composition of elements transferred from the solution to the solid phase. Increasing pH generally enhances precipitation due to the greater availability of hydroxide and carbonate ions. In addition, impurities such as Si, Ca, Ti, and Zr were also detected in the precipitates, indicating co-precipitation and the entrainment of matrix components during the process. Therefore, the process is more accurately described as REE co-precipitation rather than selective neodymium separation. pH adjustment and precipitating agent selection play important roles in controlling the yield and composition of REE precipitates; however, further purification steps are required to obtain individual REE elements with higher selectivity.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Fusi Alkali, Logam Tanah Jarang, Terak Timah Alkali Fusion, Rare Earth Element, Tin Slag
Subjects:	T Technology > TN Mining engineering. Metallurgy T Technology > TN Mining engineering. Metallurgy > TN688 Hydrometallurgy
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	El Fatih Hafidz Choirurrizal
Date Deposited:	01 Aug 2026 02:02
Last Modified:	01 Aug 2026 02:02
URI:	http://repository.its.ac.id/id/eprint/141560