ADSORPSI-DESORPSI GAS CO2 DAN H2 PADA ZEOLIT-X BERPENDUKUNG SERAT GELAS

LARASATI, ZARAH SABRINA (2016) ADSORPSI-DESORPSI GAS CO2 DAN H2 PADA ZEOLIT-X BERPENDUKUNG SERAT GELAS. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1412100109-Undergraduate_theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Pada penelitian ini bertujuan untuk meneliti adsorpsidesorpsi gas CO2 dan H2 dalam zeolit-X berpendukung serat gelas pada suhu 30°C, 40°C, dan 50°C. Zeolit-X berpendukung serat gelas disintesis menggunakan metode hidrotermal pada suhu 100°C selama 120 jam. Hasil menunjukkan bahwa kristalinitas zeolit-X berpendukung serat gelas sebesar 88,16% dan kristal zeolit-X menempel pada permukaan serat gelas. Setelah itu, zeolit-X berpendukung serat gelas diuji kapasitas adsorpsi dalam gas CO2 dan H2 pada variasi suhu 30˚C, 40˚C, dan 50˚C dengan tekanan 1 bar. Hasil menunjukkan bahwa kapasitas adsorpsi gas CO2 pada variasi suhu tersebut berturut-turut sebesar 24,64%; 15,34%; dan 12,48% berat, sedangkan jumlah CO2 yang dilepaskan kembali pada suhu variasi suhu tersebut berturut-turut adalah 76,60%; 83,62%; dan 89,58 % berat. Kemudian, untuk pengukuran kapasitas penyimpanan gas H2 pada suhu 30°C, 40°C, dan 50°C pada tekanan 1 bar berturut-turut sebesar 4,94%; 3,13%; dan 2,34% berat, sedangkan jumlah gas H2 yang dilepaskan pada variasi suhu tersebut berturut – turut adalah 73,68%; 80,56%; dan 92,59 % berat. ============================================================ This research aims to investigate the adsorptiondesorption of CO2 and H2 gases on zeolite-X supported on glass wool at temperature of 30°C, 40°C, and 50˚C. Zeolite-X supported on glass wool was synthesized using hydrotermal method at temperature 100°C for 120 hours. Results show that the crystallinity of zeolite-X supported on glass wool was 88,16% and the zeolite-X crystals covered the glass surface. Zeolite-X supported on glass wool was then determined its adsorption capacity of CO2 and H2 gases at temperature of 30°C, 40°C, and 50°C with pressure of 1 bar. Results indicate that the adsorption capacity of CO2 at temperature of 30°C, 40°C, and 50°C was 24.64, 15.34, and 12.48% (w), while the amount of desorption was 76.60, 83.62, and 89.58% (w). The results also indicate that the adsorption capacity of H2 at temperature of 30°C, 40°C, and 50°C was 4.94, 3.13, and 2.34% (w), while the amount of desorption was 73.68, 80.56, and 92.59% (w).

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 549.68 Lar a
Uncontrolled Keywords: Zeolit-X, serat gelas, sintesis, CO2, H2, adsorpsi, desorpsi.
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > (S1) Undergraduate Theses
Depositing User: Mrs Anis Wulandari
Date Deposited: 10 Jan 2017 04:06
Last Modified: 27 Dec 2018 02:15
URI: http://repository.its.ac.id/id/eprint/1430

Actions (login required)

View Item View Item