MODIFIKASI MONTMORILLONIT SEBAGAI FILLER MEMBRAN KOMPOSIT KITOSAN UNTUK APLIKASI DIRECT METHANOL FUEL CELL (DMFC)

CHANIFAN, M. IBROHIM (2014) MODIFIKASI MONTMORILLONIT SEBAGAI FILLER MEMBRAN KOMPOSIT KITOSAN UNTUK APLIKASI DIRECT METHANOL FUEL CELL (DMFC). Masters thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
1412201904-Master_theses.pdf - Published Version
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Telah dilakukan penelitian tentang membran komposit kitosanmontmorillonit termodifikasi untuk digunakan dalam aplikasi DMFC. Modifikasi montmorillonit dengan Na4P2O7 telah dilakukan untuk membuat montmorillonit memiliki sifat yang hampir sama dengan laponit. Montmorillonit tersebut telah diaktivasi dengan asam untuk mengubah Na4P2O7 dalam montmorillonit menjadi H3PO4 yang dapat memberikan sifat konduktivitas proton yang tinggi. Selain itu, montmorillonit tersebut juga dimodifikasi dengan γ-glikidoksi propil trimetoksi silan (GPTMS) untuk meningkatkan interaksi antara matriks kitosan dengan permukaan montmorillonit. Semakin tinggi kandungan montmorillonit termodifikasi dalam suatu membran komposit kitosan memberikan nilai konduktivitas proton yang terus meningkat untuk setiap kenaikan suhu hingga 80 °C. Hasil permeabilitas metanol yang paling rendah dimiliki oleh membran komposit kitosan dengan kandungan montmorillonit termodifikasi sebesar 10% yaitu sebesar 0,93418 x 10-7 cm2/s. Kandungan montmorillonit termodifikasi yang lebih tinggi dalam suatu membran komposit kitosan memiliki ketahanan termal yang lebih tinggi sehingga dapat digunakan dalam aplikasi DMFC. ============================================================ Has conducted research on chitosan-montmorillonite composite membrane modified for use in DMFC applications. Modification of montmorillonite with Na4P2O7 has been done to make the montmorillonite has properties similar to the Laponite. Montmorillonite has been activated with acid to convert Na4P2O7 in montmorillonite become H3PO4 that can provide high proton conductivity. In addition, the montmorillonite was also modified with γ-glikidoksi trimetoksi propyl silane (GPTMS) to improve the interaction between the surface of montmorillonite and chitosan matrix. High content of montmorillonite modified in chitosan composite membran has improved the proton conductivity at high temperature until 80 °C. Chitosan composite membrane with containing 10% montmorillonite modified has the lowest methanol permeability, 0,93 x 10-7 cm2/s. High content of montmorillonite modified in chitosan composite membran has higher thermal stability and possibility for direct methanol fuel cell.

Item Type: Thesis (Masters)
Additional Information: RTKi 573.774 Cha m
Uncontrolled Keywords: kitosan, montmorillonit, Na4P2O7, aktivasi keasaman, GPTMS, membran komposit, DMFC.
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > (S2) Master Theses
Depositing User: Mrs Anis Wulandari
Date Deposited: 10 Jan 2017 05:14
Last Modified: 10 Jan 2017 05:14
URI: http://repository.its.ac.id/id/eprint/1435

Actions (login required)

View Item View Item