Sintesis Nanopartikel Perak Menggunakan Ekstrak Serai (Cymbopogon citratus) Sebagai Reduktor Dengan Variasi Konsentrasi

Indrawan, Khalil Acyuta Hafidh (2026) Sintesis Nanopartikel Perak Menggunakan Ekstrak Serai (Cymbopogon citratus) Sebagai Reduktor Dengan Variasi Konsentrasi. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004221157-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

Nanopartikel perak merupakan salah satu nanoteknologi yang memiliki potensi besar untuk diaplikasikan di berbagai bidang, dan terdapat berbagai metode untuk proses sintesis yaitu metode fisik, metode kimia, dan metode biologi. Metode biologi dengan memanfaatkan ekstrak serai dinilai lebih ramah lingkungan dibandingkan dengan metode lainnya, dan lebih sederhana sehingga tidak bmembutuhkan biaya tinggi. Tujuan dari penelitian ini adalah mensintesis AgNP menggunakan ekstrak daun serai sebagai reduktor sekaligus mengetahui variasi konsentrasi ekstrak sebagai reduktor terhadap pertumbuhan AgNP, lalu hasil larutan dari sintesis AgNP terlihat berwarna coklat tua, lalu keberhasilan akan sintesis ditunjukkan dengan munculnya puncak absorbansi di panjang gelombang 400 – 450 nm pada analisis menggunakan spektrofotometer UV – Vis. Berdasarkan hasil analisis yang diperoleh tersebut, konsentrasi ekstrak yang terbaik untuk menghasilkan nanopartikel perak melalui reduksi Ag+menjadi Ag0 adalah 400 ppm hal tersebut dikarenakan pada hasil analisis UV – Vis menjadi puncak tertinggi diantara ketiga konsentrasi lainnya. Analisis FTIR pada AgNP terdapat gugus -OH dari poliol, gugus fungsi -C=O yang bervibrasi, -OH khusus asam karboksilat, dan adanya gugus alifatik CH serta gugus amina (–NH), kemudian hasil analisis PSA menunjukkan rata – rata ukuran partikelnya adalah sebesar 237,1 nm serta memiliki potensial zeta -12,55 mV
====================================================================================================================================
Silver nanoparticles are a nanotechnology with great potential for application in various fields, and there are several synthesis methods available, including physical, chemical, and biological methods. The biological method utilizing lemongrass extract is considered more environmentally friendly compared to other methods, and it is simpler, thus not requiring high costs. The aim of this study was to synthesize AgNPs using lemongrass leaf extract as a reducing agent, while also investigating the effect of varying extract concentrations as a reductant on AgNP growth. The resulting AgNP synthesis solution appeared dark brown in color, and the successful synthesis was indicated by the appearance of an absorbance peak at a wavelength of 400–450 nm, as analyzed using a UV–Vis spectrophotometer. Based on the obtained analytical results, the optimal extract concentration for producing silver nanoparticles through the reduction of Ag⁺ to Ag⁰ was 400 ppm, as this concentration yielded the highest peak among the three other concentrations in the UV–Vis analysis. FTIR analysis of the AgNPs revealed the presence of -OH groups from polyols, vibrating -C=O functional groups, -OH groups specific to carboxylic acids, aliphatic -CH groups, and amine groups (–NH). Furthermore, PSA analysis showed that the average particle size was 237.1 nm, with a zeta potential of -12.55 mV.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Ekstrak, Konsentrasi, Nanopartikel, Perak, Reduksi, Extract, Consentration, Nanoparticles, Silver, Reduction
Subjects:	Q Science > QD Chemistry > QD75.2 Chemistry, Analytic
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Khalil Acyuta Hafiidh Indrawan
Date Deposited:	05 Aug 2026 05:59
Last Modified:	05 Aug 2026 05:59
URI:	http://repository.its.ac.id/id/eprint/144047

Actions (login required)

View Item