Octaviani, Wulan Nur (2026) Pemanfaatan Asam Tanat sebagai Reduktor dan Stabilisator Nanopartikel Perak. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004211027_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Nanopartikel perak (AgNP) disintesis dengan metode green synthesis melalui pemanfaatan asam tanat. Asam tanat berperan sebagai agen pereduksi dan penstabil. Sintesis ini dilakukan dengan variasi konsentrasi asam tanat rendah yaitu 2, 4, 6, 8, dan 10 ppm serta pada konsentrasi asam tanat relatif tinggi yaitu 20, 30, 40, dan 50 ppm. Larutan hasil sintesis nanopartikel perak berwarna coklat. Keberhasilan sintesis AgNP ditunjukkan pada terbentuknya nilai absorbansi pada panjang gelombang 400-417 nm yang dianalisis dengan spektrofotometer UV-Vis. Absorbansi larutan hasil sintesis diperoleh tertinggi dengan asam tanat 40 ppm yang disertai kestabilan juga tinggi. Analisis FTIR pada AgNP ditunjukkan dengan asam tanat yang teradsorpsi pada permukaan AgNP dengan adanya vibrasi peregangan pada puncak 1325 – 1383 cm-1 yang terjadi pada gugus COO-. Hasil PSA yang diperoleh yaitu pada ukuran 66,58 – 104,2 nm menunjukkan termasuk ukuran nanopartikel dalam ukuran hidrodinamik. Analisis dilanjutkan dengan XRD yang menampilkan puncak sudut yang sesuai pada puncak khas logam perak pada sudut 2θ = 38, 44, 64 dan 78° sesuai dengan struktur FCC.
==================================================================================================================================
Silver nanoparticles (AgNPs) were synthesized via a green synthesis method using tannic acid, which acted as both a reducing and stabilizing agent. The synthesis was conducted using low tannic acid concentrations (2, 4, 6, 8, and 10 ppm) and relatively high concentrations (20, 30, 40, and 50 ppm). The resulting silver nanoparticle solution was brown in color. Successful AgNP synthesis was confirmed by absorbance readings in the 400–417 nm wavelength range, analyzed using a UV-Vis spectrophotometer. The highest absorbance accompanied by high stability—was achieved using a tannic acid concentration of 40 ppm. FTIR analysis indicated that tannic acid was adsorbed onto the AgNP surface, evidenced by stretching vibrations in the 1325–1383 cm⁻¹ range associated with the COO⁻ group. Particle Size Analysis (PSA) results showed a size range of 66.58–104.2 nm, confirming the particles fell within the nanoparticle size range (hydrodynamic diameter). Subsequent XRD analysis revealed diffraction peaks corresponding to the characteristic peaks of metallic silver at 2θ angles of 38, 44, 64, and 78°, consistent with a face-centered cubic (FCC) structure.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Nanopartikel Perak, Asam Tanat, Reduksi, Stabilitas, Sintesis. Silver Nanoparticles, Tannic Acid, Reduction, Stability, Synthesis.
Subjects:	Q Science > QD Chemistry > QD1 Oxidation-reduction reaction.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Wulan Nur Octaviani
Date Deposited:	05 Aug 2026 09:17
Last Modified:	05 Aug 2026 09:17
URI:	http://repository.its.ac.id/id/eprint/144091

Actions (login required)

View Item