Perilaku Workability Self-Compacting Geopolymer Concrete (Scgc) Mutu 42 MPA Menggunakan Metode Pencampuran Kering Berbasis Fly Ash Tipe C Dengan Variasi Superplasticizer

Putri, Nabila Shafa Aulia (2022) Perilaku Workability Self-Compacting Geopolymer Concrete (Scgc) Mutu 42 MPA Menggunakan Metode Pencampuran Kering Berbasis Fly Ash Tipe C Dengan Variasi Superplasticizer. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 10111810013011-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Seiring dengan peningkatan kemajuan teknologi konstruksi, ditemukan perkembangan revolusioner yang berkaitan dengan material baru yang murah dan ramah lingkungan sebagai alternatif pengganti semen portland. Penggunaan semen portland perlu dikurangi karena produksi semen sebagai bahan pengikat beton menyumbang gas emisi CO2 di dunia sebanyak 7% dalam setiap produksinya, yang berdampak buruk pada lingkungan. Untuk mengurangi emisi gas CO2 akibat pembuatan semen portland, digunakanlah semen geopolimer yang berbahan dasar fly ash. Semen geopolimer adalah salah satu semen hasil temuan dan dipopulerkan oleh Prof. Josefh Davidovits, semen geopolimer merupakan sintesa dari bahan alam non organik lewat proses polimerisasi. Bahan baku utama yang diperlukan untuk pembuatan semen geopolimer adalah bahan-bahan yang banyak mengandung unsur-unsur silika (SiO2) dan alumina (Al2O3). Fly ash dibagi menjadi 2 yaitu high-calcium fly ash dan low-calcium fly ash. Pada umumnya low-calcium fly ash banyak dimanfaatkan karena karakteristiknya yang bagus untuk beton geopolimer, sehingga menyebabkan keberadaan high-calcium fly ash sangat melimpah dan menjadi limbah yang berbahaya bagi lingkungan.
High-calcium fly ash sangat jarang digunakan karena tingginya kadar kalsium pada fly ash menyebabkan waktu pengerasan beton geopolimer terlalu cepat, oleh karena itu dalam penelitian ini dilakukan menggunakan metode pencampuran kering untuk memperpanjang waktu pengerasan beton dan meningkatkan kualitas beton geopolimer. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan superplasticizer terhadap workability dan kuat tekan beton SCGC, serta mengetahui komposisi dan kadar superplasticizer beton SCGC yang optimum untuk mendapatkan workability dan kuat tekan beton mutu tinggi. Metode penelitian tugas akhir ini menggunakan metode pencampuran kering, dimana bahan kimia alkali aktivator dalam bentuk padatan (NaOH dan Na2SiO3) digiling bersamaan dengan bahan pozzolan (fly ash), sehingga menghasilkan suatu butiran halus mirip semen. Terdapat 5 tahap dalam penelitian ini yaitu persiapan material penyusun, pembuatan mix design, pembuatan semen geopolimer, pembuatan beton SCGC, dan uji kuat tekan beton. Fokusan yang dilakukan pada tugas akhir ini yaitu pembuatan mix design beton SCGC dengan penambahan superplasticizer berupa Sika Viscocrete 3115n (tipe F) sebesar 0%, 1%, 3%, 5%,dan 7%. dan mengunci molaritas 14M dengan rasio Na2SiO3: NaOH sebesar 1:1. Pengujian yang dilakukan meliputi uji slump flow test, V-funnel test, L-Box test, dan uji kuat tekan beton pada usia 7, 14 dan 28 hari. Penambahan superplasticizer Sika Viscocrete 3115n sebesar 5% menunjukkan pengaruh yang signifikan terhadap workability beton SCGC dengan hasil uji Slump Flow untuk flow ability sebesar 615 mm yang telah memenuhi syarat EFNARC 2005 dengan
standar 550-850 mm, hasil uji V-funnel T0 menit untuk filling ability adalah 10 detik, dan hasil uji –Box untuk passing ability mendapatkan rasio nilai sebesar 0,83. Hasil kuat tekan beton berhasil mencapai 42,4 MPa pada umur 28 hari. Beton dapat dikatakan beton SCGC mutu tinggi karena nilai kuat tekan diatas 42 MPa.
====================================================================================================================================
Along with the increasing progress of construction technology, revolutionary developments have been found relating to new materials that are cheap and environmentally friendly as an alternative to portland cement. The use of portland cement needs to be reduced because the production of cement as a concrete binder contributes 7% of the world's CO_2 emissions in each production, which has a negative impact on the environment. To reduce CO_2 gas emissions due to the manufacture of portland cement, geopolymer cement based on fly ash is used. Geopolymer cement is one of the cements invented and popularized by Prof.
Josefh Davidovits, geopolymer cement is a synthesis of non-organic natural materials through a polymerization process. The main raw materials needed for the manufacture of geopolymer cement are materials that contain a lot of elements of silica (SiO_2) and alumina (Al_2 O_3). Fly ash is divided into 2, namely high-calcium fly ash and low-calcium fly ash. Ingeneral, low-calcium fly ash is widely used because of its good characteristics for geopolymer
concrete, causing the presence of high-calcium fly ash to be very abundant and become waste that is harmful to the environment. High-calcium fly ash is rarely used because the high calcium content in fly ash causes the hardening time of geopolymer concrete to be too fast, therefore in this research, dry mixing method was used to extend the hardening time of concrete and improve the quality of geopolymer concrete.
This study aims to determine the effect of adding superplasticizer to the workability and compressive strength of SCGC concrete, and to determine the optimum composition and superplasticizer content of SCGC concrete to obtain workability and compressive strength of high-strength concrete. The research method in this final project uses dry mixing method, in which alkaline activator chemicals in solid form (NaOH and Na2SiO3) are ground together with pozzolanic material (fly ash), so as to produce a fine grain similar to cement. There are 5 stages in this research, namely the preparation of the constituent materials, the
manufacture of mix designs, the manufacture of geopolymer cement, the manufacture of SCGC concrete, and the compressive strength test of the concrete. The focus of this final project is making SCGC concrete mix design with the addition of a superplasticizer in the form of Sika Viscocrete 3115n (type F) of 1%, 3%, 5%, and 7%. and lock the molarity of 14M with a Na2SiO3:NaOH ratio of 1:1. The tests carried out included the slump flow test, Vfunnel
test, L-Box test, and the compressive strength test of concrete at the age of 7, 14 and 28 days.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Dry mixing, High-calcium fly ash, Self Compacting Geopolymer Concrete, Superplasticizer, Workability, High-calcium fly ash, Self Compacting Geopolymer Concrete, Superplasticizer, Workability
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA439 Lightweight concrete. High strength concrete. T Technology > TD Environmental technology. Sanitary engineering > TD427.F58 Fly ash
Divisions:	Faculty of Vocational > 22301-Civil Infrastructure Engineering (D4)
Depositing User:	- Davi Wah
Date Deposited:	19 Aug 2026 01:52
Last Modified:	19 Aug 2026 02:26
URI:	http://repository.its.ac.id/id/eprint/144301

Actions (login required)

View Item