PENGARUH RASIO SiO2/Al2O3 PADA SINTESIS ZSM-5 DAN AKTIVITAS KATALITIKNYA UNTUK REAKSI ESTERIFIKASI

BARIYAH, UMMU (2014) PENGARUH RASIO SiO2/Al2O3 PADA SINTESIS ZSM-5 DAN AKTIVITAS KATALITIKNYA UNTUK REAKSI ESTERIFIKASI. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
1412201003-Master_Theses.pdf - Published Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

ZSM-5 dengan rasio mol SiO2/Al2O3 yang berbeda yaitu 25, 50, 75 dan 100 telah berhasil disintesis dari kaolin tanpa pra-perlakuan sebagai sumber silika dan alumina serta ludox sebagai sumber silika tambahan. Padatan dikarakterisasi dengan teknik difraksi sinar-X (XRD), spektroskopi inframerah (IR), adsorpsi piridin, dan scanning electron microscopy (SEM). Hasil XRD dan IR menunjukkan bahwa rasio mol SiO2/Al2O3 berpengaruh terhadap fasa dan kristalinitas dari ZSM-5. Morfologi dan ukuran partikel yang diamati dengan SEM menunjukkan hasil yang serupa, yaitu berbentuk bulat yang bergabung membentuk aglomerasi dengan ukuran partikel sekitar 1-2 μm. Data adsorpsi piridin menunjukkan bahwa semua sampel ZSM-5 memiliki sisi asam Lewis dan Brønsted. Aktivitas katalitik ZSM-5 telah dipelajari pada esterifikasi asam lemak bebas dalam minyak kemiri sunan. Besarnya konversi asam lemak bebas tertinggi sekitar 57,95% dan diketahui bahwa reaksi mengalami kesetimbangan setelah 15 menit. ============================================================ ZSM-5 with different SiO2/Al2O3 molar ratios i.e. 25, 50, 75 and 100 were synthesized from kaolin without treatment and ludox as alumina and silica source. The solids were characterized using X-ray diffraction (XRD), infrared spectroscopy (IR), scanning electron microscopy (SEM), and pyridine adsorption techniques. XRD and IR results showed that SiO2/Al2O3 molar ratio effect on the phase and crystallinity of ZSM-5. The morphology and particle size showed similar results, which are joined to form a spherical agglomeration with particle size of about 1-2 μm, as confirmed by SEM. Pyridine adsorption data showed all samples of ZSM-5 have both Lewis and Brønsted acid sites. The catalytic activity of ZSM-5 catalyst were studied in the esterification of kemiri sunan oil. The amount of free fatty acid conversion about 57,95% and the reaction reached equilibrium after 15 minutes.

Item Type: Thesis (Masters)
Additional Information: RTKi 541.395 Bar p
Uncontrolled Keywords: ZSM-5, rasio SiO2/Al2O3, keasaman, reaksi esterifikasi
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > (S2) Master Theses
Depositing User: Mrs Anis Wulandari
Date Deposited: 10 Jan 2017 07:02
Last Modified: 10 Jan 2017 07:02
URI: http://repository.its.ac.id/id/eprint/1444

Actions (login required)

View Item View Item