Pengaruh Proses Perlakuan Panas Terhadap Kekerasan dan Struktur Mikro Baja AISI 310S

Susanto, Edwin Setiawan (2009) Pengaruh Proses Perlakuan Panas Terhadap Kekerasan dan Struktur Mikro Baja AISI 310S. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 2705100013-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (15MB)

Abstract

Heat exchanger adalah suatu alat yang digunakan untuk menurunkan temperatur kerja. Bahan atau material yang dipakai untuk membuat heat exchanger biasanya adalah material yang memiliki ketahanan panas yang tinggi. Salah satu contoh bahan yang dapat dipakai untuk heat exchanger adalah stainless steels. Kegagalan pada heat exchanger yang terbuat dari stainless steels yang dioperasikan pada temperatur 1100°C dapat berupa terjadinya benjolan pada heat exchanger dan heat exchanger sudah rusak sebelum waktu yang ditentukan.
Perlakuan panas adalah kombinasi operasi pemanasan dan pendinginan terhadap logam atau paduan dalam keadaan padat dengan waktu tertentu, dimaksudkan untuk memperoleh sifat tertentu. Perlakuan yang digunakan adalah normalizing dan hardening dengan variasi temperatur 1050°C dan 1075°C. Sifat yang didapat adalah naiknya tingkat kekerasan sehingga material tersebut memiliki atau memperoleh sifat tahan aus yang tinggi, kekuatan, fatigue limit atau strength yang lebih baik, dan memperhalus butir, dalam beberapa hal juga dapat menaikkan machinability. Pengujian menggunakan uji kekerasan Vickers, karakterisasi material menggunakan XRD serta mikroskop optik. Dari hasil penelitian yang telah dilakukan diperoleh harga kekerasan maksimal pada spesimen dengan perlakuan panas hardening pada temperatur 1075°C sebesar 175HV30 dan kekerasan terendah pada spesimen dengan perlakuan panas normalizing pada temperatur 1050°C sebesar 138HV30. Dari hasil pengujian struktur mikro didapatkan struktur sigma (FeNi) dan presipitat karbida (M23C6) di dalam matriks austenit. Dan dari hasil pengujian difraksi sinar-X didapatkan fasa Chromium Iron Nickel Carbon (FeCr₀,₂₉Ni₀,₁₆C₀,₀₆). Fasa lain yang terbentuk adalah FeNi dan Cr₂₃C₆.
==================================================================================================================================
Heat exchanger is the machine that is used to change the working temperature. The material that is used to make a heat exchanger is a material that has high heat resistance. One of the materials that can be used to make a heat exchanger is stainless steel. One of the failures in a heat exchanger made from stainless steel and operated at a temperature of 1100°C is the appearance of bulges on the heat exchanger, and the heat exchanger may fail before its expected service life.
Heat treatment is the combination of heating and cooling operations applied to steel in a solid condition for a certain period of time, intended to obtain certain characteristics. The treatments used are normalizing and hardening with temperature variations of 1050°C and 1075°C. The characteristics obtained include increased hardness, resulting in higher wear resistance, better strength and fatigue limit, grain refinement, and, in some conditions, improved machinability. The testing used a Vickers hardness test, while material characterization was carried out using XRD and optical microscopy.
From the experiment that was conducted, the maximum hardness value was obtained in the specimen subjected to hardening heat treatment at a temperature of 1075°C, with a hardness of 175 HV30, while the minimum hardness value was obtained in the specimen subjected to normalizing heat treatment at a temperature of 1050°C, with a hardness of 138 HV30. From the microstructure examination, a sigma structure (FeNi) and precipitated carbides (M23C6) were found in the austenite matrix. From the X-ray diffraction analysis, the Chromium Iron Nickel Carbon phase (FeCr₀.₂₉Ni₀.₁₆C₀.₀₆) was identified. Other phases formed were FeNi and Cr₂₃C₆.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	perlakuan panas, kekerasan fasa, struktur mikro, heat treatment, hardness, phas.~, micro structure.
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	magang .
Date Deposited:	24 Sep 2026 02:05
Last Modified:	24 Sep 2026 02:05
URI:	http://repository.its.ac.id/id/eprint/144858