Pembuatan Dan Karakterisasi Membran Kitosan Serta Aplikasinya Untuk Pemisahan Deterjen Dalam Limbah

Santoso, Kurniasari (2006) Pembuatan Dan Karakterisasi Membran Kitosan Serta Aplikasinya Untuk Pemisahan Deterjen Dalam Limbah. Masters thesis, Institut Teknologi Sepuluh November.

Text 1404201003-Master_thesis.pdf Restricted to Repository staff only Download (34MB)

Abstract

Pada penelitian ini, membran kitosan dibuat dengan melarutkan serbuk kitosan dengan variasi 2 gram, 2,5 gram, dan 3 gram dalam 100 mL asam asetat 0,75% (v/v). Proses pencetakan membran dilakukan melalui tahap inversi fasa dengan membiarkan pelarutnya menguap di udara terbuka selama 3 hari sampai 20 hari. Ketebalan membran diukur menggunakan mikrometer sekrup dan diperoleh tebal rata-rata sebesar 0,05 mm. Karakterisasi membran dilakukan dengan menentukan nilai fluks dan efisiensi rejeksi terhadap larutan deterjen menggunakan sistem dead-end dengan variasi tekanan operasi 3 kgf/cm², 4 kgf/cm², dan 5 kgf/cm², serta analisis morfologi membran dilakukan dengan Scanning Electrone Microscope (SEM). Dari hasil penelitian diketahui bahwa nilai fluks dan efisiensi rejeksi yang optimum ditunjukkan oleh membran yang dibuat dengan kadar kitosan 2,5 gr/100 mL dan dioperasikan pada tekanan 3 kgf/cm². Pada kondisi tersebut, nilai fluks rata-rata yang diperoleh adalah 87,442 L/m².hari dan efisiensi rejeksi 91,09%. Aplikasi membran kitosan kondisi optimum untuk pemisahan deterjen dalam limbah menghasilkan nilai fluks 61,147 L/m².hari dan efisiensi rejeksi 97,89%.
=====================================================================================================================================
In this research, chitosan membranes have been prepared by dissolving 2 grams, 2.5 grams, and 3 grams chitosan which respectively in 100 mL acetic acid 0.75% (v/v). The mold process of membranes was carried out using inversion phase steps and exposing the solvent to the air for 3 until 20 days. The membranes' thickness was measured using micrometer sekrup and average thickness around 0.05 mm was observed. The chitosan membranes were characterized by measuring the flux and rejection efficiency toward detergent solution using dead-end module, with variation of operating pressures of 3 kgf/cm², 4 kgf/cm², 5 kgf/cm² respectively and by analyzing the morphology of membrane using Scanning Electrone Microscope (SEM). The result showed that the optimum flux value and rejection efficiency were observed on the membrane prepared from 2.5 grams chitosan/100 mL acetic acid 0.75% (v/v) and used with operating pressure of 3 kgf/cm². On that conditions, the average flux was 87,442 L/m².day with rejection efficiency of 91,09%. The application of the membrane for separating detergent in waste water showed the flux of 61,147 L/m².day and rejection efficiency of 97,89%.

Item Type:	Thesis (Masters)
Additional Information:	RTKi 660.284 24 San p
Uncontrolled Keywords:	membran Kitosan, pemisahan deterjen, nilai fluks, efisiensi rejeksi, chitosan membrane, separating detergent, flux, rejection efficiency
Subjects:	T Technology > TP Chemical technology > TP159.M4 Membranes (Technology)
Divisions:	Faculty of Mathematics and Science > Chemistry > 47101-(S2) Master Thesis
Depositing User:	magang .
Date Deposited:	02 Oct 2026 06:29
Last Modified:	02 Oct 2026 06:29
URI:	http://repository.its.ac.id/id/eprint/145189

Actions (login required)

View Item