Studi Perbandingan Katalis AI-MCM-41 dari Abu Layang Batubara PT. Ipmomi Paiton dan Sodium Metasilikat Sebagai Pendukung Katalis ZnBr2/AI-MCM-41

Ma’rifaturrizah, Ma’rifaturrizah (2010) Studi Perbandingan Katalis AI-MCM-41 dari Abu Layang Batubara PT. Ipmomi Paiton dan Sodium Metasilikat Sebagai Pendukung Katalis ZnBr2/AI-MCM-41. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 1402100031-Undergraduate_thesis.pdf Restricted to Repository staff only Download (58MB)

Abstract

Kandungan silika yang tinggi pada abu layang batubara berpotensi dimanfaatkan sebagai bahan baku dalam sintesis katalis. Ekstrak silika dari abu layang batubara yang diperoleh dengan fiisi alkali dibandingkan dengan sodium metasilikat untuk sintesis katalis Al-MCM-41 dengan rasio Si/Al 40 dan ZnBrVAl-CM-41. Katalis Al-MCM-41 disiapkan dengan metode hidrotermal pada suhu 100°C selama 144 jam. Hasil karakterisasi menggunakan XRD dan FT-IR menunjukkan bahwa seluruh katalis memiliki kesamaan difraktogram XRD dan spektra FT-IR dari MCM-41. Pengukuran keasaman katalis dengan FT-IR piridin menunjukkan bahwa seluruh katalis memiliki sisi asam Lewis dan sisi asam Bronsted. Tingkat keasaman katalis hasil sintesis adalah sebagai berikut : Al-MCM-41 (S) < Al-MCM-41 (CFA) < ZnBr2/Al-MCM-41 (S 8) < ZnBr2/Al-MCM-41 (S 16) < ZnBr2/Al-MCM-41 (CFA 8) < ZnBr2/Al-MCM-41 (CFA 16).
====================================================================================================================================
The high sillica content of Coal fly ash has potential used as raw material in catalyst synthesis. Silica extract of coal fly ash obtained from alkali fusion was compared with sodium metasillicate for the synthesis of Al-MCM-41 with Si/Al ratio 40 and ZnBr2/Al-MCM-41 catalyst. The Al-MCM-41 catalyst were prepared by hydrothermal method at 100°C for 144 hours. The characterization results using XRD and FT-IR showed that all resulting catalysts had the same XRD diffractogram and FT-IR spectra with MCM-41. Measurement of acidity catalyst with pyridine FT-IR indicated that all catalysts had Lewis and Bronsted acid sites. The order of acidity was as follows : Al-MCM-41 (S) < Al-MCM-41 (CFA) < ZnBr2/Al-MCM-41 (S 8) < ZnBr2/Al-MCM-41 (S 16) < ZnBr2/Al-MCM-41 (CFA 8) < ZnBr2/Al-MCM-41 (CFA 16).

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Abu layang batubara, Jusi alkali, sodium metasilikat, keasaman, ZnBr/Al-MCM-41, coal fly ash, alkali fusion, sodium metasillicate, acidity, ZnBr/Al-MCM-41
Subjects:	Q Science > QD Chemistry > QD481 Chemical structure.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis