Pengaruh Komposisi Abu Layang Jenis F pada Komposit Polipropilen-Abu Layang terhadap Sifat Mekanik dan Ketahanan Kimia

Harminto, Mareta (2009) Pengaruh Komposisi Abu Layang Jenis F pada Komposit Polipropilen-Abu Layang terhadap Sifat Mekanik dan Ketahanan Kimia. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 1403100038-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (3MB)

Abstract

Telah diteliti pembuatan polimer komposit yang memasukkan antara bahan polimer PP sebagai matriks dan bahan aditif anorganik yang berasal dari sisa pembakaran batu bara yang biasa dikenal dengan abu layang jenis F dari PT PLTU Asam-Asam di Kalimantan Selatan. Paduan ini bertujuan untuk mengetahui pengaruh abu layang sebagai material filler dalam plastik PP terhadap sifat ketahanan kimia dari material plastik PP tersebut serta mengetahui komposisi maksimum Sifat mekanik dari suatu polimer plastik dapat ditingkatkan dengan menambahkan filler abu layang tersebut. Peningkatan sifat mekanik yang terjadi dapat diketahui baik dari kekerasan, kekuatan polimer, modulus, kepadatan serta dapat diketahui dari ketahanan suatu plastik terhadap aksi kimia (Chemical Resistance). Semakin bertambahnya kandungan suatu filler abu layang dalam polimer plastik, maka derajat penggembungan (Swelling Degree) yang diperoleh semakin kecil. Analisis ini dilakukan dalam waktu 24 jam, 96 jam dan 168 jam. Derajat penggembungan maksimum yang terjadi sebesar 2,05% terjadi pada reagen Tetrahidrofuran.
====================================================================================================================================
A composite polymer synthesis which is a combination of polypropylene as matrix and inorganic additive of the coal combustion generally known as fly ash from PT PLTU Asam-Asam in South Kalimantan was observed. This composite is intended to determine the influence of fly ash type F as filler material in PP plastic to chemical resistance of the PP plastic material and the maximum composition as well. Mechanical properties of polymer plastic can be increased by adding the fly ash filler. The increase of the mechanical properties can be determined by its hardness, strength, modulus, solidity and its resistance to chemical reaction. The higher the fly ash filler in polymer plastic, the lower the swelling degree. This analysis was carried out in 24 hr, 96 hr and 168 hr. The maximum swelling degree of 2,05% was obtained with tetrahydrofuran reagent.

Item Type:	Thesis (Other)
Additional Information:	RSKi 620.192 Har p
Uncontrolled Keywords:	Kata Kunci: Filler, Chemical resistance, PP (polipropilen), Swelling Degree, Filler, Chemical resistance, PP (polypropilene), Swelling Degree
Subjects:	Q Science > QD Chemistry > QD481 Chemical structure.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis