Huda, Miftachul (2010) Pembuatan Elektroda Pembanding Ag/AgCl dengan Menggunakan Membran Komposit Karbon-Rotan. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 1406100061-Undergraduate_thesis.pdf Restricted to Repository staff only Download (56MB)

Abstract

Telah dibuat elektroda pembanding Ag/AgCl yang ukurannya lebih kecil dari pada elektroda pembanding Ag/AgCl komersial (Metrohm) dengan menggunakan membran komposit karbonrotan berperekat parafin. Variasi perbandingan parafin:karbon yang digunakan adalah 1:9; 2:8; 3:7; 4:6; 5:5; 6:4; 7:3 dan 9:1. Kinerja dari elektroda pembanding ini diamati menggunakan potensiotat dengan mengukur K4[Fe(CN)6], Pengukuran dilakukan menggunakan sistem tiga elektroda yaitu elektroda emas sebagai elektroda kerja, elektroda pembanding Ag/AgCl, dan elektroda platina sebagai elektroda bantu. Dilakukan juga variasi waktu pengukuran yaitu pada jam ke 0, 3, 6, dan 24. Voltamogram yang diperoleh dibandingkan dengan voltamogram hasil pengukuran elektroda Ag/AgCl komersial menggunakan uji signifikansi (uji F dan uji t) untuk menentukan kinerja elektroda pembanding Ag/AgCl yang dibuat. Nilai varian pada setiap variasi waktu pengukuran menunjukkan bahwa elektroda pembanding Ag/AgCl buatan sendiri bersifat stabil. Nilai rata-rata E setiap variasi komposisi menunjukkan perbedaan. Hal ini menunjukkan bahwa terdapat pengaruh komposisi membran terhadap nilai E.
======================================================================================================================================
Ag/AgCl Reference electrodes that smaller than the Ag/AgCl commercial reference electrode (Metrohm) using carbon- rattan composite membrane with adhesive paraffin were made. Performance of this electrode was observed using a potensiotat during measurement of K4Fe(CN)6]. Measurement was conducted using three electrodes system which is comprised of gold as a working electrode, Ag/AgCl as a reference electrode, and platinum as an auxiliary electrode. The varied time of the measurements was applied (0, 3, 6, and 24 hours). The voltammogram of the electrode which have been made, were compared to the Ag/AgCl commercial reference electrode using significance test (F test and t test) to determine performance of Ag/AgCl reference electrode that were made. The value of the variance at each varied time measurements indicated that Ag/AgCl homemade reference electrode was stable. The average value of E was different for each variation of membrane composition. This indicated that membrane compositions had close influence to E value.

Item Type:	Thesis (Other)
Additional Information:	RSKi 541.372 4 Hud p
Uncontrolled Keywords:	Ag/AgCl, membran, signifikansi, varian, Ag/AgCl, membrane, signification, varians.
Subjects:	Q Science > QD Chemistry > QD481 Chemical structure.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	magang .
Date Deposited:	19 Oct 2026 01:37
Last Modified:	19 Oct 2026 01:37
URI:	http://repository.its.ac.id/id/eprint/145658

Actions (login required)

View Item