Eco-Briquette dari Komposit Kulit Kopi, Lumpur IPAL PT SIER, dan Sampah Plastik LDPE

Sudarsono, Putri Eka Rizki (2010) Eco-Briquette dari Komposit Kulit Kopi, Lumpur IPAL PT SIER, dan Sampah Plastik LDPE. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 3305100021-Undegraduate_Thesis.pdf Restricted to Repository staff only Download (26MB)

Abstract

Bahan organik yang berasal dari sampah pertanian, seperti kulit kopi, dapat dimanfaatkan sebagai salah satu sumber alternatif energi. Kulit kopi dapat dimanfaatkan sebagai salah satu bahan campuran briket karena nilai kalornya yang cukup tinggi, yaitu 4.346,16 kal/g. Demikian pula dengan bahan organik yang berasal sisa pengolahan limbah industri, seperti lumpur IPAL PT SIER. Telah diketahui bahwa plastik memiliki nilai kalor yang tinggi. Tujuan dari penambahan sampah plastik sebagai salah satu bahan baku briket adalah untuk meningkatkan nilai kalor komposit briket dari kulit kopi dan lumpur. Tujuan lain dari penambahan plastik adalah untuk mengurangi volume sampah plastik. Tujuan dari penelitian ini untuk mengetahui pengaruh komposisi dan karakteristik eco-briquette yang paling baik dari komposit kulit kopi, lumpur IPAL, dan sampah plastik LDPE. Variabel yang digunakan dalam penelitian ini berupa metode dalam proses pembuatan briket dan komposisi briket. Digunakan metode karbonisasi dan non karbonisasi untuk komposisi kulit kopi, lumpur IPAL dan sampah plastik LDPE. Parameter yang digunakan dalam penelitian ini berupa uji mutu, analisa biaya briket, dan uji emisi. Hasil penelitian menunjukkan bahwa K1 yang memiliki komposisi 32% plastik LDPE, 48% lumpur karbonisasi dan 20% kulit kopi karbonisasi memiliki nilai kalor yang tinggi, yaitu 5.416,28 kal/g. Hasil uji emisi menunjukkan bahwa emisi dari eco-briquette K1 lebih rendah dari komposisi briket yang lain. Hasil dari kedua penelitian ini menunjukkan bahwa eco-briquette K1 adalah komposisi briket terbaik. Biaya yang diperlukan dalam pembuatan eco-briquette briket K1 adalah sebesar Rp 3.226,45/kg.
======================================================================================================================================
Organic matter from agricultural waste, such as coffee husk, can be used as a source of renewable energy. Coffee husk can be used as a briquette material because of its high energy content value, it is 4.346,16 kcal/g. Organic matter from industrial activities, such as WWT sludge, can be used as briquette material. It is already known that plastic has high energy content. This study added plastic waste as a briquette material for increasing energy content from briquette composit of coffee husk and sludge. The other purpose of plastic added is reducing amount of plastic waste. The aims of this research are analyzing the influence of composition and characteristic from the best eco-briquette with coffee husk, WWT sludge, and LDPE plastic waste. Variables used for this research were the method of briquetting process and briquette composition. Carbonization and non carbonization were the method used to made eco-briquette from coffee husk, WWT sludge, and LDPE plastic waste. Parameters used for this research were briquette quality test, cost product, and emission test. This research shows that K1 which composition of 32% plastic LDPE, 48% carbonization sludge and 20% carbonization coffee husk has high energy content of 5.416,28 kcal/g. The other result of this research shows emission of eco-briquette K1 is lower than other composition of briquette. Both of these result show that eco-briquette K1 is the best briquette composition. Cost product needed for producing eco-briquette K1 is Rp 3.226,45/kg.

Item Type:	Thesis (Other)
Additional Information:	RSL 662.6 Sud e
Uncontrolled Keywords:	eco-briquette, kulit kopi, lumpur IP AL PT SIER sampab plastik LDPE, eco-briquette, coffee husk, sludge WWT PT SIER, and LDPE plastic waste
Subjects:	T Technology > TP Chemical technology > TP315 Fuel
Divisions:	Faculty of Civil, Environmental, and Geo Engineering > Environmental Engineering > 25201-(S1) Undergraduate Theses
Depositing User:	Gunawan .
Date Deposited:	26 Oct 2026 07:01
Last Modified:	26 Oct 2026 07:01
URI:	http://repository.its.ac.id/id/eprint/145858