Analisa Sifat Mekanik Beton Geopolimer Dengan Bahan Dasar Fly Ash Dan Larutan NaOH Dengan Molaritas 12 M Dan 14 M Sebagai Aktifator

Permana, Wira Ekha (2008) Analisa Sifat Mekanik Beton Geopolimer Dengan Bahan Dasar Fly Ash Dan Larutan NaOH Dengan Molaritas 12 M Dan 14 M Sebagai Aktifator. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 3103100072-Undergraduate_thesis (1).pdf Restricted to Repository staff only Download (55MB)

Abstract

Saat ini terdapat beton geopolimer yang dapat diusulkan untuk dapat digunakan sebagai alternatif baru selain beton konvensional. Terdapat beberapa hal yang membedakan antara beton geopolimer dan beton konvensional, diantaranya yaitu bahan dasar yang digunakan. Beton geopolimer dalam tugas akhir ini menggunakan fly ash sebagai bahan dasarnya. Untuk dapat menghasilkan beton geopolimer dengan kuat tekan yang direncanakan, perlu dilakukan penelitian di laboratorium untuk mencari komposisi campuran yang tepat. Molaritas dari aktifator, kandungan air dalam campuran, perawatan (curing), temperatur pada saat curing, dan jenis alkaline yang digunakan merupakan beberapa faktor yang mempengaruhi perilaku dan kuat tekan beton geopolimer. Dalam pembuatan beton geopolimer ini menggunakan suatu aktivator alkalin sebagai pereaksinya. Aktivator yang digunakan yaitu Sodium Silikat ($Na_2SiO_3$) dan Sodium Hidroksida (NaOH). Sodium Hidroksida yang digunakan yaitu Sodium Hidroksida dengan molaritas 12 M dan 14 M, dan juga menggunakan perbandingan antara Sodium Silikat dan Sodium Hidroksida yang bervariasi, yaitu 0,5; 1; 1,5; 2; 2,5. Komposisi yang tepat dari bahan-bahan yang ada serta proses curing yang tepat dalam pembuatan beton geopolimer diharapkan mampu menghasilkan beton yang memiliki perilaku mekanis yang memuaskan.Kata Kunci: Beton geopolimer, Fly ash, Molaritas, Sodium Silikat, Sodium Hidroksida, Aktifator alkalin.
=============================================================================================================================
This time there are geopolymer concrete which can be recommended to use as a new alternative beside conventional concrete. There are many things which differentiate between conventional concrete and geopolymer concrete, one of them is based ingredients which are used. Geopolymer concrete in this final project used fly ash as based ingredients. To produce geopolymer concrete with designed strength, it needs to do research in a laboratory to find out the right composition. Molarity of activator, water content in mixed design, curing, temperature of curing, and type of alkaline activator which are used are some factors which influence mechanical properties and strength of geopolymer concrete.

To make geopolymer concrete, it needs to use alkaline activator as reacted activator. Used activators are Sodium Silicate and Sodium Hydroxide. Used Sodium Hydroxide are 12 M and 14 M molarity of Sodium Hydroxide and also used mass comparison between Sodium Silicate and Sodium Hydroxide varied between 0.5 to 2.5.

The right composition of mixed design and right curing process in making geopolymer concrete hopefully produce concrete which has good mechanical properties.

Item Type:	Thesis (Other)
Additional Information:	RSS 620.136 Per a 2008
Uncontrolled Keywords:	Concrete ; Polymer - Impregnated Concrete
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA681 Concrete construction
Divisions:	Faculty of Civil Engineering and Planning > Civil Engineering > 22201-(S1) Undergraduate Thesis
Depositing User:	magang .
Date Deposited:	28 Oct 2026 07:42
Last Modified:	28 Oct 2026 07:42
URI:	http://repository.its.ac.id/id/eprint/145976

Actions (login required)

View Item