SINTESIS ZEOLIT-X BERPENDUKUNG GLASSWOOL DENGAN VARIASI SUHU DAN WAKTU HIDROTERMAL UNTUK ADSORPSI GAS KARBON DIOKSIDA

DEVIANTI, VIKA AYU (2014) SINTESIS ZEOLIT-X BERPENDUKUNG GLASSWOOL DENGAN VARIASI SUHU DAN WAKTU HIDROTERMAL UNTUK ADSORPSI GAS KARBON DIOKSIDA. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1412201022-Master_theses.pdf] Text
1412201022-Master_theses.pdf - Published Version
Restricted to Repository staff only

Download (3MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mendapatkan zeolit-X menggunakan material
pendukung serat untuk adsorpsi gas karbon dioksida. Serat yang digunakan adalah
glass wool yang diaktivasi terlebih dulu menggunakan NaOH 4M selama 24 jam
dalam suhu ruang. Selanjutnya glasswool yang telah teraktivasi dan larutan gel
zeolit disintesis menggunakan metode hidrotermal sederhana pada variasi waktu
selama 10 jam, 15 jam, 25 jam, dan 35 jam serta suhu 90 ℃, 110 ℃, 130 ℃ dan
150 ℃. Material hasil sintesis ini kemudian dianalisis dengan teknik difraksi
sinar-X (XRD), Scanning Electrone Microscopy (SEM), dan metode adsorpsidesorpsi
Nitrogen. Pengukuran kapasitas adsorpsi karbon dioksida dilakukan
menggunakan metode gravimetri. Adsorpsi karbon dioksida dilakukan pada suhu
kamar selama 100 menit dengan aliran hidrogen 20 mL/menit. Hasil penelitian ini
menunjukkan bahwa zeolit berpendukung material serat dengan waktu kristalisasi
25 jam pada suhu 110 ℃ (ZXS 25) memiliki derajat kristalinitas paling tinggi.
Kapasitas adsorpsi karbon dioksida pada ZXS 25 mencapai 4,9% berat.

============================================================

The aim of this research is to obtain zeolite-X material for capturing carbon
dioxide by using fiber support. The fiber used in this research is NaOH activated
glasswool for 24 hours at room temperature. Then, activated glasswool and
zeolite gel solutions hydothermally were treated at 90 ℃, 110 ℃, 130 ℃ dan 150
℃ for 10 h, 15 h, 25 h, and 35 h. Afterwards, the synthesized materials were
analyzed using X-Ray Diffraction (XRD), Scanning Electrone Microscopy (SEM),
and nitrogen adsorption desorption. Carbon dioxide adsorption capacity was
determined by gravimetric method. The adsorption capacity measurement was
performed at room temperature and pressure for 100 minutes at carbon dioxide
flow of 20 mL/minutes. The results showed that the highest cristalinity and the
largest surface area were obtained at hydrothermal time of 25 hours, which has
4,9% CO2 gas adsorption.

Item Type: Thesis (Masters)
Additional Information: RTKi 545.68 Dev s
Uncontrolled Keywords: Zeolit-X, Serat, Glass wool, kapasitas adsorpsi karbon dioksida
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > 47101-(S2) Master Thesis
Depositing User: Anis Wulandari
Date Deposited: 11 Jan 2017 04:21
Last Modified: 11 Jan 2017 04:21
URI: http://repository.its.ac.id/id/eprint/1471

Actions (login required)

View Item View Item