STUDI EKSPERIMEN DAN ANALISA LAJU KEAUSAN PADA MATERIAL ALTERNATIF DENGAN DENGAN PELUMASAN PASTA PADA ROTARY VALVE MESIN PEMBUAT PASTA

AZHARI, SUBHAN KEMAL (2016) STUDI EKSPERIMEN DAN ANALISA LAJU KEAUSAN PADA MATERIAL ALTERNATIF DENGAN DENGAN PELUMASAN PASTA PADA ROTARY VALVE MESIN PEMBUAT PASTA. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2112106022-undergraduate thesis.pdf]
Preview
Text
2112106022-undergraduate thesis.pdf - Published Version

Download (3MB) | Preview

Abstract

Setiap peralatan yang bergerak selalu mengalami kerusakan. Hal ini dikarenakan adanya dua benda yang saling berkontak atau gesekan. Permasalahan yang dialami oleh satu industri adalah sering terjadi kebocoran pada mesin pembuat pasta yaitu pada rotary valve yang sebelumnya sudah pernah dijadikan tugas akhir oleh mahasiswa teknik mesin ITS. Dalam tugas akhirnya tersebut dia merekomendasikan material polytetrafluoroethylene (PTFE) yang memiliki specific wear rate yang jauh lebih baik apabila dibandingkan dengan material yang digunakan sebelumnya yaitu polyoxymethylene (POM). Namun masih ada material – material lain yang bisa jadi material alternative yang diharapkan memiliki life time serta wear rate coefficient yang lebih baik.
Langkah-langkah penelitian yang dilakukan adalah sebelum dilakukan pengujian pada mesin tribometer, terlebih dahulu spesimen uji direndam dengan menggunakan pasta gigi pepsodent whitening untuk mengetahui pengaruh pasta terhadap material uji. Setelah direndam, spesimen uji ditimbang dengan menggunakan timbangan digital. Setelah itu dilakukan pengujian dengan menggunakan mesin tribometer dengan menggunakn pembebanan konstan yaitu 8 kg dan 3 variasi kecepatan yaitu pada speed control 50 (38,7 rpm), 60 (44,4 rpm) dan 70 (52,3 rpm). Pengujian dilakukan dengan menggunakan pelumas berupa pasta pepsodent whitening. Sebelum pengujian dimulai, dilakukan penimbangan massa awal spesimen uji yaitu massa setelah spesimen uji direndam dengan pasta gigi dan kalibrasi alat yaitu speed control dan load. Pengulangan pengujian dilakukan sebanyak 3 kali sesuai dengan speed control yang ditetapkan. Setelah pengujian dilakukan foto mikro dan analisa struktur permukaan.
Hasil pengujian didapatkan bahawa material alternative Ultra high molecular weight polyethylene ( UHMWPE ) memiliki nilai specific wear rate yang lebih baik dibandingkan material Nylon dimana pada rpm 38,7 UHMWPE memiliki specific wear rate 3x lebih baik daripada Nylon, rpm 44,4 4x lebih baik dan rpm 52,5 10x lebih baik. Nilai specific wear rate juga mempengaruhi life material, dimana pada rpm 38,7 life time UHMWPE 4x lebih baik dari Nylon, pada rpm 44,4 9x lebih baik dan pada rpm 52,3 12x lebih baik
"============================================================================================="
Any equipment that moves always damaged. This is because the two objects come into contact or rub against each other. Problems experienced by one industry are often leak on machine of pasta makers that is on the rotary valve that has previously been used as a final examination by a student of mechanical engineering ITS. In the final examination she recommended material polytetrafluoroethylene (PTFE), which has a specific wear rate is much better when compared with the previously used material is polyoxymethylene (POM). But there is still others material that could be an alternative material that is expected to have a life time and wear rate coefficient better.
Steps before the research is conducted testing on Tribometer machine, first test specimen is immersed by using Pepsodent toothpaste whitening pastes to determine the effect of the test material. After soaking, the test specimens were weighed using a digital scale. After it was examined by using a machine Tribometer with constant loading is 8 kg and 3 variations in speed control the speed of which 50 (38.7 rpm), 60 (44.4 rpm) and 70 (52.3 rpm). Tests carried out using a lubricant such as Pepsodent whitening paste. Before the test begins, weighing is done the initial mass is the mass of the test specimen after the test specimens soaked with toothpaste and calibration tools that speed and load control. Repetetion done 3 times in accordance with the speed control set. After testing done micro photo and surface structure analysis.
Result of tests on material alternative obtained Ultra high molecular weight polyethylene ( UHMWPE ) has specific wear rate yang much better than Nylon material which in rpm 38,7 UHMWPE has specific wear rate 3x better than Nylon, rpm 44,4 4x better and rpm 52,5 10x better. Specific wear rate also influence material life time, which in rpm 38,7 life time UHMWPE 4x better than Nylon, in rpm 44,4 9x better than rpm 52,3 12x better.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 620.112 92 Azh s
Uncontrolled Keywords: material alternative, lubrikasi, wear rate
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Users 13 not found.
Date Deposited: 13 Jan 2017 07:10
Last Modified: 26 Dec 2018 03:34
URI: http://repository.its.ac.id/id/eprint/1534

Actions (login required)

View Item View Item