Analisis Pengaruh Variasi Waktu Tahan dan Media Pendingin Proses Hardening pada Sifat Kekerasan Baja Aisi 8655 sebagai Solusi Kegagalan pada Hammer Crusher

Ramadhan, Yudha Prakasa Putra (2017) Analisis Pengaruh Variasi Waktu Tahan dan Media Pendingin Proses Hardening pada Sifat Kekerasan Baja Aisi 8655 sebagai Solusi Kegagalan pada Hammer Crusher. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2713100064-Undergraduate_Theses.pdf - Published Version

Download (5MB) | Preview

Abstract

Hammer crusher merupakan alat untuk menghancurkan terak (clinker) yang telah di proses dalam kiln dan telah didinginkan pada clinker cooler. Hammer crusher sering terjadi keausan yang sangat cepat dan tidak sesuai dengan umur pakainya. Dalam penelitian ini dilakukan analisa kegagalan penyebab terjadinya kegagalan pada hammer crusher dan solusi agar komponen tidak mudah aus. Pengujian yang dilakukan untuk menganalisis material ini adalah uji komposisi, metalografi, dan hardness. Dari uji komposisi didapatkan material hammer crusher berkesesuaian komposisinya dengan AISI 8655. Kemudian pada material ini dilakukan proses hardening pada temperatur 850oC dengan waktu tahan 30 menit dan 60 menit, yang kemudian di quench dengan media pendingin udara, oli, dan air untuk meningkatkan kekerasannya dan meningkatkan ketahanan aus nya. Setelah di hardening, komponen di uji impak, hardness, dan metalografi untuk dibandingkan pada kondisi awalnya. Hasil percobaan ini diperoleh bahwa kekerasan komponen meningkat dari yang semula 243 BHN menjadi 400-550 BHN. Diperoleh kekerasan yang paling besar pada proses hardening dengan waktu tahan 30 menit dengan menggunakan media pendingin air yaitu sebesar 552 BHN. =========================================================================================== Hammer crusher is a tool to destroy the slag (clinker) which has been process in the kiln and cooled at the clinker cooler. The hammer crusher often wear very quickly and not in accordance with that lifetime. In this research, failure analysis of Hammer Crusher and modification was performance so that components are not easy to wear. Test that used for this material composition test (OES), metallography and hardness. The result from the composition test shown the composition hammer crusher is similar with AISI 8655. Then the hardening process is carried out at a temperature of 850°C with a holding time of 30 minutes and 60 minutes, which next quenched with air, oil, and water to increase its hardness and wear resistance. After the hardening, the components are tested with impact test, hardness and metallography to compare it’s with the prior condition before hardening. The results of this experiment showed that the hardness value of the component increased from 243 BHN into 400-550 BHN. The maximum hardness value there on hardening with holding time of 30 minutes and the cooling water is equal to 552 BHN.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Hammer Crusher, AISI 8655, Hardening, Hardness
Subjects: T Technology > TN Mining engineering. Metallurgy
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: YUDHA PRAKASA PUTRA RAMADHAN
Date Deposited: 27 Feb 2017 03:18
Last Modified: 05 Mar 2019 03:13
URI: http://repository.its.ac.id/id/eprint/1641