Pengaruh variasi temperatur dan waktu Holding Sintering terhadap Sifat Mekanik dan Morfologi Biodegradable Material Mg-Fe-Zn dengan Metode Metalurgi Serbuk untuk Aplikasi Orthopedic Devices

Nurrohman, Hamid (2017) Pengaruh variasi temperatur dan waktu Holding Sintering terhadap Sifat Mekanik dan Morfologi Biodegradable Material Mg-Fe-Zn dengan Metode Metalurgi Serbuk untuk Aplikasi Orthopedic Devices. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2713100006-Undergraduate-Theses.pdf]
Preview
Text
2713100006-Undergraduate-Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Dewasa ini telah dikembangkan biodegradable material yang berguna untuk implant tulang. Biodegradable material berbasis paduan Mg telah banyak diteliti dengan menggunakan metode pengecoran. Salah satu kelemahan pengecoran adalah menghambat proses osifikasi karena material yang terbentuk tidak berporos. Penelitian ini bertujuan untuk mengembangkan biodegradable material berbasis paduan Mg dengan penambahan unsur Fe dan Zn. Dengan menggunakan metode metalurgi serbuk. Dengan metode ini diharapkan paduan yang terbentuk memiliki struktur berpori sehingga proses osifikasi pada awal tumbuhnya tulang dapat berjalan dengan baik. Parameter penelitian ini adalah temperatur sinter dan waktu tahan. Temperatur sinter yang digunakan adalah 200, 250, dan 300 oC. dan waktu tahannya selama 30, 60, dan 90 menit. Pengujian mekanik menggunakan uji tekan dan uji kekerasan. Pengujian peluruhan menggunakan metode weight loss. Dari penelitian yang telah dilakukan didapatkan paduan Mg-Fe-Zn yang sesuai dalam sifat mekanik dan morfologi adalah paduan Mg-Fe-Zn temperatur sintering 300o C dan waktu holding mencapai 90 menit. Didapatkan senyawa utama penyusun paduan adalah MgZn. Didapatkan nilai kekerasan dan keukatan tekan paduan secara berturut-turut 135 Mpa dan 205 Mpa, serta nilai laju peluruhan sebesar 2.46 cm/tahun.

=========================================================================================

Nowadays biodegradable material has been developed for bone implant application. Biodegradable material Mg based alloy has been researched by casting method. One of the weakness in this
method is hamper ossification process. This research has purpose
to develop biodegradable material Mg based with addition of Fe
and Zn. In order to develope porous structure and to increase
ossification process, powder metallurgy method was used.
Parameter of this experiment were sintering temperature and
holding time. Sintering temperature were 200, 250 and 300 oC,
and the holding time were 30, 60, and 90 minutes. The samples
were characterized using compression and hardness test.
Degradation test using weight loss method. Based on the result,
sintering temperature 300 oC and holding time 90 minutes with has suitable for bone implant were match with mechanical
properties and the morphology. Results of experiment show that hardness is 135 Mpa and compressive strength is 205 Mpa . In addition the degradation rate of alloy is 2.46 cm/year.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: biodegradable material; Mg-Fe-Zn; orthopedic device; Metalurgi Serbuk; sintering
Subjects: T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis