Pemanfaatan Limbah Serbuk Kayu Sebagai Campuran Polyurethane Pada Insulasi Palka Kapal Ikan Tradisional

Hidayat, Mochamad (2017) Pemanfaatan Limbah Serbuk Kayu Sebagai Campuran Polyurethane Pada Insulasi Palka Kapal Ikan Tradisional. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 4214106005-Undergraduate_Theses.pdf]
Preview
Text
4214106005-Undergraduate_Theses.pdf

Download (2MB) | Preview

Abstract

alam proses penangkapan ikan sangat dibutuhkan beberapa perlengkapan seperti alat penangkap ikan, instrumentasi dan palka/tempat penyimpanan sementara ikan. Nelayan tradisional yang melautnya one day fishing biasanya hanya membawa es balok. Polyurethane adalah buih plastik padat campuran larutan Polyol dan Isocynate yang biasa digunakan sebagai bahan insulator pada tempat penyimpanan. Dari hasil pengamatan limbah penggergajian yang dihasilkan menjadi serbuk kayu per gelondong dengan diameter 30 cm dan panjang 1 m dengan 5 kali penggergajian, tebal gergaji 0,8 cm dihasilkan 0,0088 m³/ gelondong hanya dibuang atau dibakar. Oleh karenanya dibutuhkan uji konduktivitas termal untuk campuran serbuk kayu dan polyurethane dengan berbagai variasi perbandingan takaran. Penambahan serbuk kayu maksimum dapat dilakukan adalah 40% dari total volume bahan campuran, yaitu polyurethane dan serbuk kayu karena bahan komposit (serbuk kayu-polyurethane) tidak dapat berikatan dengan baik sehingga mudah terpisah dari bentuk lempengan asalnya. Koduktivitas termal insulator yang baik dan ekonomis pada penambahan 40% serbuk kayu (0.05252 W/m°C) dan mampu mempertahankan 2 kg es kristal hingga mencair sempurna pada 34 jam. Keuntungan secara ekonomis dalam pembuatan insulasi sebesar 4,8 m³ dengan pengaplikasian komposit didapatkan sebesar Rp 4.486.000 dibanding dengan pembuatan insulasi 100% Polyurethane pada volume yang sama.
====================================================================================== In the process of fishing it takes some supplies such as fishing equipment, instrumentation and storage of fish. The
traditional fishermen of their fishing days fishing usually only bring ice cubes. Solid plastic polyurethane foam is a mixture solution of polyols and isocyanates, commonly used as an insulating material storage. From the observation waste
generated being sawmill sawdust per spindle with diameter of 30 cm and a length of 1 m with 5 times sawmill, Saws 0.8 cm thick produced 0.0088 m³ / burnable logs only discarded. Therefore takes thermal conductivity test to review mixture of sawdust and
polyurethane comparison with variations different dosing.
Maximum disposals sawdust can be done is 40% of the total volume of material mixture, polyurethane and sawdust because composite material (sawdust-polyurethane) can not be bond with good so easy slab separately from origin form. Thermal Conductivity insulating good and economical on disposals 40% wood flour (0.05252 W / m°C) and is able to maintain a 2 kg of ice crystals melt up perfect on 34 hours. Operating profits economical from 4,8m³ insulation composite application with obtained Rp 4.486.000
compared with 100% Polyurethane Insulation Manufacture.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Serbuk kayu; Composites; Polyurethane; Insulation; Thermal Conductivity
Subjects: T Technology > T Technology (General)
T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Marine Technology (MARTECH) > Marine Engineering > 36202-(S1) Undergraduate Thesis
Depositing User: - MOCHAMAD HIDAYAT
Date Deposited: 10 Mar 2017 09:26
Last Modified: 10 Mar 2017 09:26
URI: http://repository.its.ac.id/id/eprint/2855

Actions (login required)

View Item View Item