EKSPERIMEN PROSES PRODUKSI INSOLUBLE SULFUR BERBAHAN BAKU SULFUR PADAT DENGAN PROSES POLIMERISASI PADA TEMPERATUR 250 - 350 C

WATI, RISKA RIYA and AFIFAH, MEITA (2017) EKSPERIMEN PROSES PRODUKSI INSOLUBLE SULFUR BERBAHAN BAKU SULFUR PADAT DENGAN PROSES POLIMERISASI PADA TEMPERATUR 250 - 350 C. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2314106006-2314106017-Undergraduate_Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Di dalam industri manufaktur karet, soluble sulfur merupakan vulcanizing agent yang ternyata masih belum dapat menghasilkan karet dengan kualitas yang baik karena masih dapat menyebabkan terjadinya sulfur blooming, dan untuk mengatasinya soluble sulfur ini perlu dirubah menjadi insoluble sulfur. Insoluble sulfur adalah sulfur yang tidak terlarut dalam carbon disulfide (CS2). Insoluble sulfur banyak digunakan sebagai vulcanizing agent pada industri manufaktur karet. Vulcanizing agent merupakan bahan yang berguna untuk meningkatkan kekuatan, ketahanan, dan mengurangi sifat lengket serta bau dari produk karet itu sendiri. Proses produksi insoluble sulfur melibatkan banyak variabel proses polimerisasi. Sehingga diperlukan penelitian lebih lanjut untuk mendapatkan hasil produk yang maksimal. Penelitian ini bertujuan untuk mendapatkan data pengaruh temperatur dan lama waktu pemanasan konstan terhadap kemurnian dan yield produk insoluble sulfur secara eksperimen. Adapun penelitian ini menggunakan sulfur fase vapor dengan alat reaktor yang belum menghasilkan produk dan sulfur fase liquid dengan cawan porselen. Didapatkan hasil fase liquid optimal pada variabel temperatur 250°C untuk yield 49,39% dan untuk kemurnian pada 300°C sebesar 68,21%. Sedangkan lama waktu konstan optimal didapatkan pada pemanasan 30 menit untuk kemurnian 80,08% dan 0 menit (tidak dilakukan pemanasan konstan) untuk yield 49,39%. Dalam proses analisanya, analisa langsung dan analisa setelah 1 hari mempengaruhi penurunan kemurnian berkisar 22%. =============================================================================================================== In the rubber-making industry, soluble sulfur as vulcanizing agent has not been able to produce rubber with good quality because it can cause sulfur blooming, and to overcome this problem it can be converted into insoluble sulfur. Insoluble sulfur is sulfur which is insoluble in carbon disulfide. The most important use of insoluble sulfur is as vulcanizing agent in the rubber-making industry. Vulcanizing agent is a material which is used to improve strength, resiliency, freedom from stickiness and odor of rubber products. Process production of insoluble sulfur involves many process variables of polymerization. So, it’s needed further research to obtain the maximum product yield. This research aims to get experimentally data of the effect of temperature and time constant on the purity and yield. As for those study using sulfur vapor phase by means of reactor that has not produced the product and sulfur liquid phase with porcelain bowl. Optimal result obtained liquid phase at a variable temperature of 250°C to yield 49,39% and for purity at 300°C by 68,21%. While the optimal length of time constant is obtained on heating of 30 minutes to a purity of 80,08 % and 0 minutes (without constant heating) to yield 49,39 %. In the process of analysis after one day affect the decrease in the purity reaches 24%.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Insoluble Sulfur, Kemurnian, Polimerisasi, Vulcanizing Agent, Yield
Subjects: T Technology > TP Chemical technology > TP1140 Polymers
T Technology > TP Chemical technology > TP156 Crystallization. Extraction (Chemistry). Fermentation. Distillation. Emulsions.
Divisions: Faculty of Industrial Technology > Chemical Engineering > (S1) Undergraduate Theses
Depositing User: RISKA RIYA WATI
Date Deposited: 25 Jan 2017 06:26
Last Modified: 06 Mar 2019 07:06
URI: http://repository.its.ac.id/id/eprint/3208

Actions (login required)

View Item View Item