AMOBILISASI KATION Cd2+ PADA GEOPOLIMER BERBAHAN DASAR ABU LAYANG PT. IPMOMI

MAHMUDAH, I’IS ANISATUN (2016) AMOBILISASI KATION Cd2+ PADA GEOPOLIMER BERBAHAN DASAR ABU LAYANG PT. IPMOMI. skripsi thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1410100006-Abstrak.pdf] Text
1410100006-Abstrak.pdf - Published Version
Restricted to Repository staff only
Download (198kB) | Request a copy
[thumbnail of 1410100006-Conclusion.pdf] Text
1410100006-Conclusion.pdf - Published Version
Restricted to Repository staff only
Download (185kB) | Request a copy
[thumbnail of 1410100006-Undergraduate_Theses.pdf] Text
1410100006-Undergraduate_Theses.pdf - Published Version
Restricted to Repository staff only
Download (1MB) | Request a copy

Abstract

Pada penelitian ini telah dilakukan amobilisasi kation Cd2+
pada geopolimer dengan bahan dasar abu layang PT. IPMOMI.
Penambahan Al(OH)3 dilakukan untuk memvariasikan
SiO2/Al2O3 pada geopolimer Rasio SiO2/Al2O3 sebesar 6,46
diketahui menghasilkan geopolimer dengan kuat tekan tertinggi yaitu 25 MPa. Komposisi tersebut digunakan sebagai komposisi geopolimer untuk amobilisasi kation Cd2+. Geopolimer dengan penambahan kation Cd2+ sebesar 4000 ppm (mg/kg abu layang) menghasilkan kuat tekan yang tertinggi yaitu 38,6 MPa. Sampel geopolimer Cd-1000 merupakan sampel yang terbaik untuk mengamobilisasi Cd2+ daripada sampel yang lainnya. Penambahan ion Cd2+ lebih dari 1000 ppm menyebabkan lebih banyak ion Cd2+ yang ter-leaching.

Item Type: Thesis (skripsi)
Uncontrolled Keywords: Abu layang; Amobilisasi Kation Cd 2+; Geopolimer; Leaching; Mikrostruktur
Subjects: Q Science
Divisions: Faculty of Engineering, Science and Mathematics > School of Chemistry
Depositing User: Anis Wulandari
Date Deposited: 10 Jun 2016 18:17
Last Modified: 03 Sep 2025 03:29
URI: http://repository.its.ac.id/id/eprint/331

Actions (login required)

View Item View Item