Pemanfaatan Bahan Magnetik (Fe3o4) Berbahan Dasar Karat Besi Hasil Korosi Atmosferik Sebagai Radar Absorber Material.

Alwi, Muhammad Faisol (2017) Pemanfaatan Bahan Magnetik (Fe3o4) Berbahan Dasar Karat Besi Hasil Korosi Atmosferik Sebagai Radar Absorber Material. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 1112100052_Undergraduate_Theses.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Karat besi merupakan produk oksida yang dihasilkan dari logam besi. Fenomena terbentuknya karat pada mekanisme korosi tidak bisa dihindari sehingga membuat bahan logam cepat rusak dan mudah terdegradasi. Karat besi mengandung beberepa senyawa diantaranya FeO, Fe2O3 dan Fe3O4 yang terbentuk karena interaksi pertukarsn ini oleh Base Metal dengan lingkungan disekitarnya. Oleh karena itu, dilakukan penelitian dengan judul pemanfaatan bahan magnetik (Fe3O4) berbahan dasar karat besi hasil korosi atmosferik sebagai radar absorber material. Penelitian ini bertujuan untuk mengetahui kemampuan karat besi di wilayah surabaya, malang, dan bangkalan dalam menyerap gelombang serta mengetahui tipe magnetisasi serbuk karat besi. Penelitian dilakukan dengan metode sparasi menggunakan magnet permanen sebesar 0,02 T dengan variasi lingkungan surabaya, malang dan Bangkalan. Berdasarkan karakterisasi XRD didapatkan bentuk fasa pada semua daerah adalah fasa Fe3O4 dengan tipe amorphus. Pada karakterisasi XRF diketahui bahwa unsur yang paling banyak ditemukan adalah Fe. Sedangkan berdasarkan hasil uji VNA didapatkan bahwa pada frekuensi yang sama, besar reflection loss pada produk korosi yang didapat di daerah malang sebesar -12 dB, di bangkalan sebesar -7,8 dB, sedangkan di daerah surabaya sebesar -20,8 dB.
Kata Kunci :Karat besi, Fe3O4, Material Penyerap Radar, VNA
===============================================================================================
Iron rust is an oxide product from iron metal. The
phenomenon of rust formation on corrosion mechanism can’t
be avoided so makes metal material corrupting and degraded
easily. Iron rust contains of several compound which is able to
be used as radar wave absorber material, including FeO,
Fe2O3 and Fe3O4 which was determined by evironmental
condition around of base metal. Hence, the research with tittle
the utilization of magnetic material (Fe3O4) based on iron rust
from atmospheric corrosion mechanism as radar absorber
material was done. This research aims to understand the
ability of rust iron in Surabaya, Malang and Bangkalan in
absorb waves and to know the magnetization type of rust iron.
The experiment was done by separation method using
permanent magnet 0,02 T from different region: Surabaya
,Malang, and Bangkalan. Based on the result of XRD test, the
phase form of whole region is Fe3O4 phase with amorphous
tipes. Fe is the most elements found in metal based on XRF
test. And based on VNA test at the same frequency, the amount
of reflection loss on corrosion product from Malang, Madura,
and Surabaya are -12 dB, -7,8 dB, -20.8 dB.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Karat besi, Fe3O4, Material Penyerap Radar, VNA
Subjects:	Q Science Q Science > QC Physics
Divisions:	Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis