Pengaruh Variasi Rasio Mol Sio2/Al2o3 Pada Tahap Feedstock Gel Dan Waktu Kristalisasi Dalam Sintesis Zeolit X Dari Kaolin Bangka Belitung Melalui Proses Leaching Asam

Maulida, Hanifatul (2017) Pengaruh Variasi Rasio Mol Sio2/Al2o3 Pada Tahap Feedstock Gel Dan Waktu Kristalisasi Dalam Sintesis Zeolit X Dari Kaolin Bangka Belitung Melalui Proses Leaching Asam. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
1413100025-Undergraduate-Theses.pdf - Published Version
Restricted to Repository staff only

Download (3MB)

Abstract

Pada penelitian ini betujuan untuk mengetahui pengaruh proses leaching pada komposisi kaolin Bangka Belitung sebagai sumber silika dan alumina, rasio SiO2/Al2O3 pada tahap feedstock gel terhadap pembentukan kristal zeolit X, dan waktu kristalisasi terhadap pembentukan fase zeolit. Zeolit disintesis melalui 2 tahapan yaitu, tahap seedgel dan tahap feedstock gel yang diikuti overall gel dan proses hidrotermal pada suhu 105 ºC. Hasil penelitian dikarakterisasi menggunakan, XRF, FTIR, XRD dan SEM-EDX. Berdasarkan sintesis yang telah dilakukan, perbedaan rasio SiO2/Al2O3 tahap feedstock gel yang diberikan mempengaruhi penggunaan bahan komersial (ludox) sebagai sumber silika pada sintesis zeolit X. Pada rasio SiO2/Al2O3 = 2 dan 3 terbentuk fase utama zeolit X yang bercampur dengan fase pengotor sodalit. Disamping itu rasio SiO2/Al2O3 = 4, terbentuk fase utama gismondin dan fase pengotor zeolit X serta fase tak teridentifikasi. Selanjutnya di pelajari lebih lanjut, pengaruh waktu kristalisasi dalam proses hidrotermal pada rasio SiO2/Al2O3 = 4, dengan waktu kristalisasi yang digunakan, 4, 6, 12, dan 24 Jam. Pengaruh waktu kristalisasi memberikan perbedaan signifikan pada fase zeolit hasil sintesis. Pada waktu kristalisasi 12 jam, zeolit mulai mengalami transformasi menjadi zeolit P. ======================================================================================================================== The purpose of this research was knowing the effect of acid leaching process on kaolin Bangka Belitung composition as silica and alumina sources, ratio SiO2 / Al2O3 in feedstock gel step, crystals X zeolite formation and crystalization time on zeolite phase formation. Zeolites were synthesized through by two step namely, seedgel and feedstock gel was followed by overall gel and hydrothermal process. The synthesis products were characterized by XRF, FTIR, XRD and SEM-EDX. The Results showed that the difference of SiO2/Al2O3 ratio affected the commercial materials (ludox) composition used for zeolite synthesis. The major of zeolite X mixed with impurity phase of sodalite were formed at ratio 2 and 3. On the other hand, The major of gismondine, impurity phase of zeolite X and unidentified phase were formed at ratio 4. Furthermore, the crystallization time effect of hydrothermal process in the SiO2/Al2O3 ratio used four variation time (4,5,12,24 hours). The crystallization time effected significantly in phase of zeolite synthesis products. On 12 hours of hydrothermal time, zeolite started to transform into zeolit P.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Zeolit X, Zeolit P, Sodalit, Kaolin, Rasio mol SiO2/Al2O3 , Waktu kristalisasi Hidrotermal
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > (S1) Undergraduate Theses
Depositing User: - Hanifatul Maulida
Date Deposited: 25 Apr 2017 07:44
Last Modified: 18 May 2017 03:28
URI: http://repository.its.ac.id/id/eprint/3953

Actions (login required)

View Item View Item