Aplikasi Tio2 Sebagai Fotokatalis Dalam Penjernihan Air Dengan Media Perekat Resin

Alfaizah, Aning Malikah (2017) Aplikasi Tio2 Sebagai Fotokatalis Dalam Penjernihan Air Dengan Media Perekat Resin. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 2412100059-Undergraduate-Thesis.pdf Restricted to Repository staff only Download (2MB)

Abstract

Penelitian ini mengenai aplikasi TiO2sebagai fotokatalis untuk menjernihkan air dengan media perekat resin.Masing-masing TiO2fasa anatase dan TiO2komersil dicampurkan pada resin dengan perbandingan komposisi TiO2sebesar 0,5 ; 1 ; 1,5 gram dan massa resin tetap 25 gram. Campuran resin dan TiO2dilapiskan pada stik es krim. Selanjutnya stik tersebut dimasukkan ke dalam 100 ml air yang telah diberi pewarna merah ponceau (Cl. 16255) dan diberi perlakuan penyinaran. Dilakukan uji absorbansi pada sampel air berwarna setelah penyinaran di bawah sinar matahari setiap 6 jam per harinya selama 48 jam (8 hari). Berdasarkan hasil pengujian yang telah dilakukan pada penelitian ini menunjukkan bahwa semakin luas lapisan TiO2 yang digunakan semakin baik kemampuannya dalam menjernihkan air. Nilai absorbansi terkecil 0,070052 untuk TiO2sintesis yaitu pada sampel dengan konsentrasi TiO2 sintesis 0,5 gram pada luasan 30,255 cm2dengan penurunan sebesar 62,8%.
==================================================================================================================
This research investigates the use of TiO2 as photocatalist to purify water with resin adhesive as the medium. Each anatase phase of TiO2 and commercil TiO2 was mixed by the resin with the composition of TiO2 namely 0,5 ; 1 ; 1,5 grams and resin mass remains 25 grams. The compound of resin and TiO2 was coated in ice stick. Then the ice stick was soaked in 100 ml of water which has been dyed by using ponceau red stain (Cl. 16255). The absorbance test was performed on the colored water sample which have been receiving sun’s radiation around 6 hours per day during 48 hours (8 days). The result of the test shows that TiO2 coating’s size affects the process of water purification, the more wider TiO2 coating size could make the water purifies well. The minimum absorbance score at 0,070052 for TiO2 syntesis was found on TiO2 syntesis by 0,5 grams concentration at 30,255 cm2 with the reduction of 62,8%.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	TiO2, fotokatalis, absorbansi, resin, penjernihan air
Subjects:	Q Science > QC Physics
Divisions:	Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User:	Users 13 not found.
Date Deposited:	10 May 2017 08:12
Last Modified:	28 Dec 2017 08:45
URI:	http://repository.its.ac.id/id/eprint/41249

Actions (login required)

View Item