Pengaruh Variabel Arah Serat Terhadap Kekuatan Bending Pada Komposit Serat Tebu Bermatriks Gypsum Dan Resin

Prakasa, Septyan Dana (2017) Pengaruh Variabel Arah Serat Terhadap Kekuatan Bending Pada Komposit Serat Tebu Bermatriks Gypsum Dan Resin. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2113030059- Non_Degree.pdf] Text
2113030059- Non_Degree.pdf - Published Version
Restricted to Repository staff only

Download (3MB)

Abstract

Serat tebu adalah bahan sisa pengolahan gula yang banyak
ditemui akan tetapi masih sedikit pemanfaatannya. Pemaanfaatan
yang sedikit membuat serat tebu tidak memiliki nilai ekonomis dan
lebih banyak di bakar untuk tungku pemanas.
Untuk membantu mengolah limbah serat tebu maka
pemanfaatan serat tebu akan di aplikasikan ke dalam campuran
komposit dengan capuran resin dan gipsum. Tujuan dari pengujian
ini adalah untuk dapat menggatikan kayu sebgaai bahan
perabotan rumah tangga.
Setelah dilakukan pengujian bending dengan metode 3
tumpuan (tree point bending) maka didapatkan kekuatan bending,
momen bending, dan modulus elastisitas. Hasil maksimal terdapat
pada komposit dengan orientaasi arah sudut serat 0º.
==================================================================================================================
Bagasse fiber is the material the rest of the sugar processing a
lot but it is still a bit of its utilization. The benefits are a little
bit make bagasse fiber has no economic value and more
in fuel to furnace heating.
To assist in processing the bagasse fiber so, its utility will
be applied into a mixture of resins and gypsum. The purpose
of this test is to wood as material becomes can the furniture.
After testing with tree point bending then obtained the power of
bending, bending moment, and modulus of elasticity. Maximum
results found in composite with fiber orientation angle
of direction of 0 degrees.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Komposit serat tebu, Serat Tebu bermatriks Resin dan Gypsum, Uji Bending.
Subjects: T Technology > T Technology (General)
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3
Depositing User: Users 13 not found.
Date Deposited: 12 May 2017 04:28
Last Modified: 28 Dec 2017 08:46
URI: http://repository.its.ac.id/id/eprint/41254

Actions (login required)

View Item View Item