Pengaruh Kebakaran Temperatur 700˚C Dan 900˚C Terhadap Perubahan Kekerasan Dan Keuletan Pada Pengelasan Material SA 36 Dengan Menggunakan Metode SMAW

Yusuf, Muhammad Andy (2016) Pengaruh Kebakaran Temperatur 700˚C Dan 900˚C Terhadap Perubahan Kekerasan Dan Keuletan Pada Pengelasan Material SA 36 Dengan Menggunakan Metode SMAW. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2112030007-Non-Degree.pdf]
Preview
Text
2112030007-Non-Degree.pdf

Download (2MB) | Preview

Abstract

Salah satu permasalahan dalam pengelasan suatu material
logam itu ialah apabila sebuah konstruksi bangunan yang
memiliki dasar berbahan logam hasil pengelasan SMAW terkena
kebakaran bertemperatur tinggi.
Pada penelitian ini akan menganalisa mengenai pengaruh
kebakaran temperatur 700˚C dan 900˚C terhadap sifat mekanis
dari material SA 36 dengan pengujian tarik yang bertujuan untuk
mengetahui daerah patahan pada spesimen, kemudian Hardness
test bertujuan untuk mengetahui kepastian titik batas antara
daerah Base Metal, HAZ, Weld Metal, juga untuk mengetahui
nilai kekerasan daerah patahan pada pengujian tarik spesimen,
dan Uji Metalografi yang bertujuan untuk mengetahui struktur
mikro pada daerah batasan Base Metal, HAZ, Weld Metal.
Dari hasil pengujian tarik, didapatkan bahwa spesimen
pengaruh kebakaran pada temperatur 700⁰C memiliki nilai
tegangan tarik lebih besar dari spesimen temperatur 900⁰C yaitu
482,70 MPa dan 443,19 MPa. Letak patahan berada pada Base
Metal dan dilihat dari betuk patahan, material bersifat ductile.
Pada hasil uji kekerasan, daerah weld metal pada spesimen
temperatur 700˚C memiliki nilai yang lebih besar dari 900˚C
yaitu 82,57 HRB dan 76,60 HRB. Sedangkan hasil pengujian
metalografi, didapat lebar HAZ pada temperatur 700˚C dan 900˚C
sebesar 2,06 mm dan 2,43 mm. Struktur mikro yang terdapat pada
material hanya terdapat ferit dan pearlite.

=============================================================================

In the construction of multi-storey building there are
several types of materials that can be used, one of which is to use
steel material. In building construction are welding process. This
welding process is very worth noting, as a result of the welding
process itself affects the mechanical properties such as toughness,
strength, and good hardness of the material and joints.
From this study will analyze the influence of heat
variations in temperature 700C and 900C of the mechanical
properties of a material with a tensile testing which aims to
determine the fault area on the specimen, then Hardness test aims
to know the boundary points between regions Base Metal, HAZ,
Weld Metal, also to determine the hardness value of the fault area
at tensile test specimens, and test Metallography which aims to
determine the microstructure in the area limits Base Metal, HAZ,
weld metal.
The results obtained from the higher temperature heat
influences the hardness of the material will decrease and tenacity
decreases, and for the region Weld Metal, the higher the
temperature the influence of heat, it will damage the metal Weld
area.

Item Type: Thesis (Diploma)
Additional Information: RSM 671.521 2 Yus p
Uncontrolled Keywords: Pengaruh kebakaran; Pengelasan SMAW; Hardness Test; Uji Tarik dan Metalography Test; Effect of Heat; Welding SMAW; Hardness Test; Tensile Test and Metalography test
Subjects: T Technology > TJ Mechanical engineering and machinery
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3
Depositing User: Anis Wulandari
Date Deposited: 02 Jun 2017 02:56
Last Modified: 28 Dec 2018 02:25
URI: http://repository.its.ac.id/id/eprint/41453

Actions (login required)

View Item View Item