Studi Sifat Mekanik Komposit Aluminium Berpenguat Nano Silika (Al/Sio2) Hasil Fabrikasi Dengan Metalurgi Serbuk

Hanafi, . (2015) Studi Sifat Mekanik Komposit Aluminium Berpenguat Nano Silika (Al/Sio2) Hasil Fabrikasi Dengan Metalurgi Serbuk. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1110201006-Master-Thesis.pdf - Published Version

Download (1MB) | Preview

Abstract

Telah dilakukan pembuatan komposit Al/SiO2 melalui metode metalurgi serbuk dengan menggunakan Aluminium komersial produk Merk-Germany sebagai matrik yang digabungkan dengan nano silika (SiO2) yang diperoleh dari hasil sintesis pasir Bancar Tuban melalui metode koopresipitasi. Fabrikasi komposit dilakukan dengan metode metalurgi serbuk dengan metode pencampuran basah (wet mixing), dengan mendium pencampur berupa larutan Butanol, sintering pada temperatur 500 oC selama 2 jam dalam vacum furnace. dan hasilnya dilakukan beberapa analisa dan uji untuk mengetahui sifatnya, yaitu analisa densitas dan porositas, uji XRD, SEM-EDX, uji kekerasan (Brinnel) dan uji tekan . Hasil penelitian menunjukkan bahwa dari analisa difraksi sinar-X diperoleh komposit Al/SiO2 pada x = 0% hingga 30% dengan fasa kristal berupa Al dan sedikit Al2O3 dan SiO2 yang ditunjukkan oleh peak yang rendah. Peningkatan fraksi volume SiO2 pada komposit cenderung menurunkan densitas dan meningkatkan porositas. Demikian pula dari hasil uji mekanik yang dilakukan, kuat luluh (Yield Strength =YS), kuat tekan maksimum (UCS) dan modulus elastis (ME) serta kekerasan bahan (BHN) cenderung mengalami penurunan dengan bertambahnya fraksi volume SiO2 diatas 5% pada komposit Al/SiO2. Nilai YS, UCS, ME dan kekerasan bahan memiliki nilai tertinggi ketika fraksi volume SiO2 dalam komposit adalah 5%. ================================================================================================================== Composites have been fabricated Al/SiO2 through powder metallurgy method using a Aluminium commercial product by Merck-Germany as matrix combined with nano silica (SiO2) obtained from the synthesis Bancar Tuban sand through koopresipitasi method. Fabrication of composites made by powder metallurgy method by the wet mixing method, using the Butanol as medium solution. Sintering at a temperature of 500° C for 2 hours in a vacuum furnace. the result exsperiments then analyzed and tested to determine its nature. There are density and porosity analyze, test XRD, SEM-EDX and test pressure (Brinnel). The results showed that of the X-ray diffraction analysis was obtained composite Al/SiO2 at x= 0 % to 30 % with a crystalline phase of Al and Al2O3 and SiO2 slightly indicated by a low peak. Increasing the volume fraction of SiO2 on composite tends to decrease density and increase porosity. Similarly, from the results of mechanical tests conducted, yield strength (YS = Yield Strength), compressive strength (CS), the maximum compressive strength (UCS) and elastic modulus (ME) and material hardness (BHN) tends to decrease with increasing volume fraction of SiO2 the composite. Value YS, CS, ME and hardness of materials has the highest value when the volume fraction of SiO2 in the composite is 5 % .

Item Type: Thesis (Masters)
Additional Information: RTFi 620.5 Han s
Uncontrolled Keywords: komposit Al/SiO2, nano komposit, aluminium, nanosilika, sifat mekanik.
Subjects: Q Science > QC Physics
Divisions: Faculty of Mathematics and Science > Physics > (S2) Master Theses