Pengaruh Penambahan Konsentrasi ZnSO4 Terhadap Ketebalan, Sifat Adhesif Dan Ketahanan Korosi Pada Baja ASTM A213 T11 Dengan Metode Elektroplating

-, Muhyidin A.M. (2016) Pengaruh Penambahan Konsentrasi ZnSO4 Terhadap Ketebalan, Sifat Adhesif Dan Ketahanan Korosi Pada Baja ASTM A213 T11 Dengan Metode Elektroplating. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2712100146-Undergraduate-Theses.pdf]
Preview
Text
2712100146-Undergraduate-Theses.pdf

Download (2MB) | Preview

Abstract

Elektroplating pada dunia industri banyak dimanfaatkan
untuk melapisi benda kerja. Metode ini dilakukan untuk
meningkatkan nilai estetika dan perlindungan terhadap ancaman
lingkungan yang menyebabkan korosi. Oleh karena itu dilakukan
penelitian yang bertujuan untuk mengetahui pengaruh
penambahan konsentrasi ZnSO4 ( 5%; 10%; 15%; 20%)
terhadap ketebalan lapisan, sifat adhesive lapisan dan ketahanan
lapisan hasil elektroplating terhadap korosi. Penelitian ini
menggunakan larutan elektrolit ZnSO4 sebagai media elektrolit
dan juga sekaligus sebagai sumber logam zink yang akan
melapisi logam. Metode yang digunakan pada penelitian ini
adalah metode elektroplating yaitu dengan menempatkan logam
lain pada permukaan logam induk yang akan dilindungi dengan
ditambahkan bahan kimia dan bantuan arus listrik. Pengujian
ketebalan di uji dengan alat DFT (Dry Film Thickness),
pengujian sifat adhesive dengan menggunakan alat PosiTest ATM
Adhesion Tester, pengujian laju korosi dengan weight lose dan
untuk melihat struktur permukaan menggunakan SEM. Hasil
pengujian menunjukan bahwa penambahan konsentrasi ZnSO4
akan menaikan ketebalan lapisan coating dan penambahan
konsentasri juga akan menaikan nilai kelekatan maksimum pada konsentrasi 15%, akan tetapi jika konsentrasi dinaikan semakin
tinggi maka kelekatan akan turun kembali serta penambahan
konsentrasi akan menurunkan laju korosi.

===============================================================================

Electroplating in the industrial is being used to coat the
surface of workpiece. This method is used to enhance the
aesthetic value and protection of environmental threats that
cause the corrosion. Therefore, this research to determine the
effect of the addition of concentration ZnSO4 ( 5%; 10%; 15%;
20%) on coating thickness, adhesive properties and the corrosion
resistance of the layer coating from electroplating. This research
used ZnSO4 solution as electrolyte medium and also as a source
of zinc metal that will coat to the surface of metal. The method
used in this research is the electroplating method with placing
zinc metal at another metal surface to be protected with the
added chemicals and an electric current. Thickness testing with
DFT (Dry Film Thickness), adhesive properties testing by using
PosiTest AT-M Adhesion Tester, corrosion resistance testing with
weight lose methode and to observe the surface structure using
scanning electron microscope. The result sof the test showed that
the addition of ZnSO4 concentration will increase the thickness of
the coating layer and and the addition of concentration also increase the value of and maximum value of adhesive
propertiesat 15% of ZnSO4, but if the concentration is increased
the higher, the adhesive values will fall back and the addition of
concentration will decrease the corrosion rate.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.112 23 Muh p
Uncontrolled Keywords: Elektroplating; Zink; ZnSO4; Korosi; Konsentrasi; Zinc; Corrosion; Concentration
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Anis Wulandari
Date Deposited: 13 Jun 2017 04:59
Last Modified: 26 Dec 2018 02:08
URI: http://repository.its.ac.id/id/eprint/41631