Sintesis Zif-8 Dengan Penambahan Al2o3 Serta Aktivitasnya Sebagai Katalis Pada Reaksi Esterifikasi Pfad (Palm Fatty Acid Distillate)

Imaninsa, Novicha (2016) Sintesis Zif-8 Dengan Penambahan Al2o3 Serta Aktivitasnya Sebagai Katalis Pada Reaksi Esterifikasi Pfad (Palm Fatty Acid Distillate). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1412100033-Undergraduate-Thesis.pdf - Published Version

Download (2MB) | Preview

Abstract

ZIF-8 (Zeolitic Imidazolate Frameworks-8) dan Al- ZIF-8 dengan variasi Al2O3 (0,6 mmol; 1,2 mmol; 4,8 mmol; 9,6 mmol dan 19,2 mmol) telah berhasil disintesis dengan metode solvotermal dalam pelarut metanol pada suhu 70 °C selama 24 jam. Difraktogram padatan hasil sintesis menunjukkan puncak karakteristik yang sama dengan ZIF-8 yaitu pada 2θ = 7,34°; 10,40°; 12,76°; 16,49° dan 18,08°. Al- ZIF-8 memiliki bentuk morfologi kotak dan terdapat penurunan jumlah Zn seiring dengan bertambahnya jumlah Al sesuai dengan hasil SEM-EDX. Pada karakterisasi FTIR, muncul puncak serapan pada 420 cm-1 yang menunjukkan adanya ikatan antara seng dan nitrogen. Stabilitas termal ZIF- 8, Al-ZIF-1,2 dan Al-ZIF-4,8 masing-masing adalah 392 °C, 519 °C and 416 °C. Padatan hasil sintesis digunakan pada reaksi esterifikasi PFAD (Palm Fatty Acid Distilled) menggunakan katalis Al-ZIF-4,8 dapat menurunkan kadar FFA 80,27 %. Hasil uji kromatografi gas menunjukkan bahwa dengan menggunakan katalis Al-ZIF-4,8 memiliki yield lebih besar (62%) dibandingkan dengan menggunakan katalis ZIF-8 (3,98%). ================================================================================================================== ZIF-8 (Zeolitic Imidazolate Frameworks-8) and Al-ZIF-8 with variation of mol Al2O3 (0,6 mmol; 1,2 mmol; 4,8 mmol; 9,6 mmol dan 19,2 mmol) have been succesfully synthesized by solvothermal method at temperature 70 °C for 24 h. Difractogram of materials had same characteristic peak with ZIF-8 exhibited at 2θ = 7,34 °; 10,40 °; 12,76 °; 16,49 ° and 18,08 °. Al-ZIF-8 had cubic structure and amount of Zn decrease along with Al increasement, based on SEM-EDX analysis. The FTIR spectra has a peak at 420 cm-1, which indicated the presence of zinc and nitrogen bonding. Stability thermal of ZIF-8, Al-ZIF-1,2 and Al- ZIF-4,8, is 392 °C, 519 °C and 416 °C, respectively. Materials used to esterification reaction of Palm Fatty Acid Distilled (PFAD) that showed significant activities, Free Fatty Acid (FFA) convertion which increased to 80.27% by using Al-ZIF-4,8 as the catalyst . Gas Chromatography Characterization of methyl ester that used Al-ZIF-4,8 catalyst showed better yield (62%) than methyl ester that used ZIF-8 catalyst (3,98%).

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 620.116 Ima s
Uncontrolled Keywords: Metal Organic Framework, ZIF-8, Al2O3, Sintesis Solvotermal, Aktivitas Katalis
Subjects: Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions: Faculty of Mathematics and Science > Chemistry > (S1) Undergraduate Theses
Depositing User: Users 13 not found.
Date Deposited: 19 Jun 2017 07:03
Last Modified: 27 Dec 2018 01:50
URI: http://repository.its.ac.id/id/eprint/41745

Actions (login required)

View Item View Item