Pengaruh Penambahan Trietilamin (Tea) Dalam Sintesis Zif-8 Dengan Metode Solvotermal

Pratiwi, Dessy Ayu (2015) Pengaruh Penambahan Trietilamin (Tea) Dalam Sintesis Zif-8 Dengan Metode Solvotermal. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1411100021-Undergraduate Thesis.pdf - Published Version

Download (2MB) | Preview

Abstract

Sintesis ZIF-8 (Zeolitic Imidazolate Frameworks-8) telah berhasil disintesis untuk mengetahui pengaruh dari penambahan trietilamin dalam kristalinitas, morfologi, dan ukuran pori dari kristal ZIF-8 dengan metode solvotermal. Sintesis dilakukan dengan mereaksikan seng nitrat dan 2-metilimidazol dalam pelarut metanol, ditambahkan dengan variasi rasio molar trietilamin yang dipanaskan pada suhu 70 °C selama 24 jam. Semakin besar rasio molar trietilamin, maka massa dari produk yang didapatkan juga semakin besar. Difraktogram XRD hasil sintesis menunjukkan puncak-puncak utama yang menunjukkan karakteristik dari ZIF-8 yaitu pada sudut 2θ = 7,3; 10,3; 12,7; 16,4, dan 18,0. Dari karakterisasi FTIR terdapat puncak pada serapan 421 cm-1 yang menunjukkan adanya ikatan seng dengan nitrogen. Dari pengukuran adsorpsi N2 diperoleh luas permukaan ZIF-8 sebesar 683,746 m2/g. Hasil analisis termal dengan TGA menunjukkan bahwa ZIF-8 hasil sintesis memiliki stabilitas termal pada suhu 340-380°C =============================================================================================== Synthesis of ZIF-8 (Zeolitic Imidazolate Frameworks-8) was prepared to investigate the influences of triethylamine (TEA) on the crystallinity, particle size, morphology of ZIF-8. Synthesis had been carried out by reaction of zinc nitrate and 2- metilimidazole and variation molar ratio of triethylamine (TEA) in methanol at 70 °C for 24 hours. The mass of ZIF-8 product increased from 1:2:1 to 1:2:8 with increasing of TEA molar ratio. Difractograms of material exhibited strong peaks at 2θ = 7,3; 10,3; 12,7; 16,4; and 18,0, which were the characteristic peaks of ZIF-8 materials. The FTIR spectra as a peak at 410 cm-1, indicated the presence of zinc bonded to the nitrogen in ZIF-8. The results of surface area by N2 adsorption method of ZIF-8 was 683,746 cm3/g for ZIF-8 1:2:2 and had thermal stability of ZIF-8 1:2:4 in the temperature range 340-380°C

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 620.116 Pra p
Uncontrolled Keywords: ZIF-8, Metanol, TEA, Karakterisasi
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > (S1) Undergraduate Theses
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 10 Jul 2017 03:49
Last Modified: 10 Jul 2017 03:49
URI: http://repository.its.ac.id/id/eprint/41937

Actions (login required)

View Item View Item