Pengaruh Thermal Cycle terhadap Ketahanan Adhesi dan Abrasif pada Pelapisan SS 304 dengan NiCrSiB Metode Flame Spray and Fused

Azhari, Muhammad Ridho (2017) Pengaruh Thermal Cycle terhadap Ketahanan Adhesi dan Abrasif pada Pelapisan SS 304 dengan NiCrSiB Metode Flame Spray and Fused. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2713100079-Undergraduate_Theses.pdf - Published Version

Download (5MB) | Preview

Abstract

Proses pelapisan logam dengan metode flame spray & fused adalah salah satu solusi untuk perlindungan material terhadap pengaruh lingkungan khususnya pada boiler. Erosi pada superheater tube yang merupakan komponen dari coal fired-boiler disebabkan oleh partikel debu (fly ash) yang berasal dari pembakaran batu bara. Penelitian ini mensimulasikan kondisi atmosfer boiler yang bekerja pada temperature tinggi dengan suatu metode thermal cycle dan bertujuan untuk menganalisis pengaruh thermal cycle pada pelapisan NiCrSiB dengan metode flame spray & fused terhadap struktur mikro dan sifat mekanik. Thermal cycle menyebabkan ketahanan abrasi meningkat yang ditunjukkan dengan nilai berat yang hilang menurun hingga 0.0251 g/cm2 pada cycle ke-10. Pada hasil SEM pengaruh thermal cycle menurunkan presentase porositas yang ada hingga mencapai 1,529% pada cycle ke-10. Uji XRD dan EDS menampilkan adanya perubahan fasa selama thermal cycle. Thermal cycle menyebabkan peningkatan kekuatan adhesi hingga 10.29 MPa pada cycle ke-10. Thermal cycle juga menyebabkan kekerasan mikro meningkat hingga 780.5 HV pada cycle ke-5 dan adanya sedikit penurunan pada cycle ke-10 menjadi 774.47 HV serta menurunkan nilai kekasaran hingga 14.72 µm pada cycle ke-10. ======================================================================================================================== Metallic coating with flame spray & fused method is a solution to protect materials from the environment, especially in boiler. Erosion occurred on superheater tube that was a component from coal-fired boiler caused by flying ash from coal combustion. The condition under boiler atmosphere that operate at high temperature is simulated by thermal cycle method on this study. The purpose of this study to analyze the effect of thermal cycle on NiCrSiB coating with flame spray & fused method on its microstructure and mechanical properties. Thermal cycle causes the abrasive resistant increase up to 0.0251 g/cm2 at 10th cycle. SEM result showed that thermal cycling decrease the porosity until 1,529% at 10th cycle. XRD and EDS test showed that there was a phase transformation during thermal cycle. During the thermal cycle the adhesive strength of the coating increase up to 10.29 Mpa at 10th of cycle. Thermal cycle causes the micro hardness increase up to 780.5 HV at 5th cycle and decrease at 10th cycle with the value of 774.47 HV. Thermal cycle also causes the surface roughness of coating decrease up to 14.72 µm at 10th cycle.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Boiler, SS 304, NiCrSiB, Thermal cycle, Daya Lekat, Ketahanan Abrasi
Subjects: Q Science > Q Science (General)
T Technology > TN Mining engineering. Metallurgy
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: Muhammad Ridho Azhari
Date Deposited: 18 Aug 2017 07:54
Last Modified: 18 Aug 2017 07:54
URI: http://repository.its.ac.id/id/eprint/42392