Pengaruh Variasi Komposisi BaM/PAni Matriks Cat Epoxy Pada Pelapisan Single Layer dan Two Layer Dengan Metode Spray Coating Untuk Aplikasi Material Penyerapan Radar

Kholid, Rifki Rachman (2017) Pengaruh Variasi Komposisi BaM/PAni Matriks Cat Epoxy Pada Pelapisan Single Layer dan Two Layer Dengan Metode Spray Coating Untuk Aplikasi Material Penyerapan Radar. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2713100075-Undergraduates_Theses.pdf - Published Version

Download (7MB) | Preview

Abstract

Penyerapan gelombang mikro dapat dilakukan melalui rekayasa material, menggunakan material RAM (RadarAbsorbing Material ) yang terdiri dari material resistif dan material magnetik untuk menyerap gelombang radar. Material magnetik yang digunakan adalah BaM (Barium Heksafferit). Sintesis material BaM menggunakan metode solid state. Material BaM di dopping dengan Zn2+ untuk meningkatkan nilai Magnetic Saturation (Ms) dari 58,97 emu/gr menjadi Ms 60,04 emu/gr dan menurunkan nilai koersivitas (Hc) dari 4743 Oe menjadi 833,17 Oe. PAni (Polianiline) merupakan material polimer konduktif yang digunakan pada penelitian ini. Material PAni didapatkan dengan proses polimerisasi oksidasi kimia. Penggunaan PAni dikarenakan memiliki stabilitas thermal dan konduktivitas listrik yang baik sebesar 1,579 x 10-5 S/cm. Komposit BaM/PAni kemudian dicampurkan dengan cat epoxy dengan variasi persen berat 5,10,15 wt%. Kemudian dilapiskan pada material alumunium 2024 dengan metode spray coating dengan lapisan single layer dan two layer. Untuk mengetahui nilai rugi refleksi dari material RAM yang telah dilapisi pada plat alumunium dilakukan pengujian VNA (Vector Network Analyzer) pada rentang frekuensi 8-12 GHz. Didapatkan nilai RL maksimum sebesar -27,153dB 9,002 GHz dengan ketebalan 100,6 micron pada komposisi BaM/PAni 15 wt% dengan lapisan two layer. Dari hasil penyerapan dan ketebalan yang didapat komposisi komposit BaM/PAni 15 wt% terhadap matriks cat epoxy sesuai untuk aplikasi RAM pada pesawat. ======================================================================================================================== Microwave absorption can be done through engineering materials using RAM ( Radar Absorbing Material ) which consists of magnetic material and resistive material to absorb radar waves. The magnetic material used is BaM (Barium M Hexaferrite). BaM material synthesized using solid state method. BaM material doped with Zn 2+ ions to increases Magnetic Saturation (Ms) value from 58.97 emu/gr to 60.04 emu/gr and reduces coercivity (Hc) from 4743 Oe to 833. 17 Oe. PAni (Polyaniline) is a conducting polymer material used in this study. PAni material was obtained by a chemical oxidative polymerization process. PAni is used because it has good thermal stability and electrical conductivity amount 1,579 x 10 - 5 S/c m. The BaM / PAni composite was mixed with epoxy paint and the variation of weight percentage ( 5, 10, dan 15 wt %). Afterwards, coated on 2024 alumunium material using spray coating method with single layer and two layers coating. To determine the reflect ion loss value of the material RAM that has been coated on the aluminum plate then VNA ( Vector Network Analyzer) tested in the frequency range of 8 to 12 GHz. Obtained a maximum R L value amount - 27.153 dB 9.002 GHz with a

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: RAM, Barium Heksaferrit, Polianilin, Matriks Cat Epoxy, Spray Coating.
Subjects: T Technology > T Technology (General)
T Technology > TN Mining engineering. Metallurgy
U Military Science > U Military Science (General)
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: - Rifki Rachman Kholid
Date Deposited: 25 Aug 2017 02:39
Last Modified: 05 Mar 2019 04:37
URI: http://repository.its.ac.id/id/eprint/42603

Actions (login required)

View Item View Item