Analisis Pengaruh Variasi Temperatur dan Waktu Tahan Tempering terhadap Sifat Kekerasan dan Ketahanan Aus Material ASTM A532 Class III Type A yang Di-hardening sebagai Solusi Kegagalan Chute Inlet Feed Liner pada Vertical Roll Mill

Maghfiroh, Qory (2017) Analisis Pengaruh Variasi Temperatur dan Waktu Tahan Tempering terhadap Sifat Kekerasan dan Ketahanan Aus Material ASTM A532 Class III Type A yang Di-hardening sebagai Solusi Kegagalan Chute Inlet Feed Liner pada Vertical Roll Mill. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2713100034-Undergraduate_Theses.pdf]
Preview
Text
2713100034-Undergraduate_Theses.pdf - Published Version

Download (9MB) | Preview

Abstract

Chute inlet feed merupakan saluran masuk feed material dari belt conveyor menuju rotary feeder pada vertical roller mill. Kondisi kerja dari bagian ini membutuhkan komponen yang memiliki kekerasan dan ketahanan aus yang tinggi agar proses dapat berlangsung dengan baik. Oleh karena itu dipasanglah liner pada chute inlet feed yang terbuat dari material yang sesuai dengan kondisi kerja. Namun liner yang digunakan masih mengalami keausan sebelum umur pakai yang diharapkan. Dalam penelitian ini dilakukan analisis penyebab terjadinya kegagalan pada chute inlet feed liner dan salah satu solusinya. Pengujian yang dilakukan dalam penelitian ini adalah pengujian komposisi, pengujian metalografi, pengujian XRD, pengujian kekerasan, dan pengujian ketahanan aus. Dari pengujian komposisi diperoleh bahwa material liner yang digunakan adalah ASTM A532 Class III Type A. Material liner ini mengalami kegagalan karena terjadinya mekanisme abrasive wear. Untuk memperbaiki sifat kekerasan dan ketahanan ausnya, kemudian dilakukan proses pemanasan pada material ini hingga temperatur 950oC dengan waktu tahan 60 menit, kemudian didinginkan dengan media pendingin oli. Lalu dilakukan proses tempering pada temperatur 200oC, 250oC, dan 300oC dengan waktu tahan 40 menit, 80 menit, dan 120 menit. Setelah proses perlakuan panas diperoleh nilai kekerasan yang paling tinggi dan nilai laju keausan yang paling rendah pada temperatur tempering 250oC dan waktu tahan 120 menit. Nilai kekerasan material liner dengan perlakuan tersebut mencapai 748,04 HV dan laju keausannya 6,01 mm/hari. Laju keausan yang rendah menunjukkan bahwa material memiliki ketahanan aus yang tinggi.
===========================================================================================================
Chute inlet feed is a chamber where the feed materials fall down from belt conveyor toward rotary feeder in vertical roller mill. This condition requires material with excellent hardness and wear resistance in order to make the process work sustainably. Therefore a liner with an appropriate material need to be assembled on chute inlet feed. However, a failure occurs even when the liner material has not attained the lifetime yet. This study investigate cause of failure on chute inlet feed liner and the alternative solution. Several examinations need to be performed, such as Optical Emission Spectroscopy (OES), metallography, XRD, hardness, and wear resistance. The OES examination shows that liner material which has been used comply with ASTM A532 Class III Type A. The failure of this liner occurs due to abrasive wear mechanism. To improve hardness and wear resistance, materials was heated to 950oC and held for 60 minutes. This process followed by oil quench. After that, tempering process was applied with various temperature (200oC, 250oC, and 300oC) and holding time (40 minutes, 80 minutes, and 120 minutes). The results show that the highest hardness value 748,04 HV and lowest wear rate 6,01 mm/day was obtained at the tempering temperature 250oC and holding time 120 minutes. Low wear rate indicate a high wear resistance.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Liner, ASTM A532 Class III Type A, Tempering, Kekerasan, Ketahanan Aus
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TS Manufactures
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Qory Maghfiroh .
Date Deposited: 10 Aug 2017 01:29
Last Modified: 05 Mar 2019 04:35
URI: http://repository.its.ac.id/id/eprint/42790