Analisa dan Simulasi Proses Sand Casting dalam Pembuatan Female Contact Resistor Berbahan Dasar Copper

Septyan, Candra Simon (2013) Analisa dan Simulasi Proses Sand Casting dalam Pembuatan Female Contact Resistor Berbahan Dasar Copper. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2713100080-Undergraduate_Theses.pdf - Published Version

Download (4MB) | Preview

Abstract

Female Contact Resistor (FCR) adalah salah satu komponen dari circuit breaker yang berfungsi sebagai penghambat/pembatas arus listrik dari suatu rangkaian listrik. FCR diproduksi dengan metode sand casting, namun banyak fenomena pada pengecoran yang tidak dapat dilihat pada eksperimennya secara langsung. Simulasi pengecoran menggunakan ANSYS Mechanical APDL dapat memperlihatkan fenomena yang terjadi dalam pengecoran FCR ini. Komponen FCR ini dibuat menggunakan material copper dan cetakannya menggunakan material pasir. Variasi pada penelitian ini adalah bentuk penampang dari runner dan riser, yaitu persegi dan lingkaran. Dari penelitian ini didapatkan hasil bentuk pada sistem saluran mempengaruhi hasil dari pengecoran. Tegangan termal yang dihasilkan pada sistem saluran dengan sprue dan riser berpenampang lingkaran sebesar 2,39E+07 Pa adalah yang terendah dan sistem saluran dengan sprue dan riser berpenampang persegi sebesar 4,71E+07 Pa adalah yang terbesar. Penyusutan yang terjadi pada sistem saluran dengan sprue dan riser berpenampang lingkaran sebesar 3164,042844 mm3 adalah yang terkecil dan sistem saluran dengan sprue dan riser berpenampang persegi sebesar 3167,249273 mm3 adalah yang terbesar. Hasil coran yang paling baik dimiliki oleh sistem saluran dengan sprue dan runner berpenampang lingkaran karena memiliki tegangan termal dan penyusutan yang lebih kecil dibandingkan yang lainnya. ======================================================================================================================== Female Contact Resistor (FCR) is one of the components of circuit breaker that functioning as an electrical current barrier or limiting electrical current from an electric circuit. FCR is produced by sand casting method, but many foundry phenomena cannot be seen in the experiment directly. Casting simulation using ANSYS Mechanical APDL can show the phenomena that occurs in this experiment. FCR component is made using copper material and the mold is using sand material. The variations in this research are the cross section of runner and riser, that is square and circle. From this research, the results of this cross-sectional shape gating system affect the outcome of the casting. The thermal stress generated from gating system using circular cross-sectional shape is 2.39E+07 Pa and from gating system using a square cross-sectional shape is 4.71E+07 Pa. Shrinkage that occurs from gating system using circular cross-sectional shape is 3164.042844 mm3 and from gating system using a square cross-sectional shape is 3167.249273 mm3. The best casting result is obtained using circular cross-sectional shape gating system because of the less thermal stress and shrinkage from the others.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Analisa Elemen Hingga, Female Contact Resistor, Tembaga, Tegangan Termal, Shrinkage, Crack
Subjects: T Technology > TS Manufactures
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: Candra Simon Septyan
Date Deposited: 12 Sep 2017 08:20
Last Modified: 12 Sep 2017 08:20
URI: http://repository.its.ac.id/id/eprint/42831

Actions (login required)

View Item View Item